本文選題：腐蝕 + 鋁合金�。� 參考：《機(jī)械工程材料》2017年12期

【摘要】：采用掃描電鏡觀察、X射線衍射分析、電化學(xué)分析等方法,結(jié)合實(shí)際服役地區(qū)大氣環(huán)境分析,研究了變電站電流互感器用6A02鋁合金接線板在沿海工業(yè)環(huán)境中的腐蝕行為及機(jī)理。結(jié)果表明:鋁合金接線板主要發(fā)生晶間腐蝕,且由晶間腐蝕向均勻腐蝕發(fā)展;腐蝕產(chǎn)物主要為鋁的硫化物和氯化物;大氣中的Cl~-和硫化物降低了鋁合金接線板的腐蝕電位,提高了腐蝕電流密度,是導(dǎo)致鋁合金接線板腐蝕失效的主要因素。
[Abstract]:The corrosion behavior and mechanism of 6A02 aluminum alloy junction board for substation current transformer in coastal industrial environment were studied by means of scanning electron microscope (SEM) observation X-ray diffraction analysis and electrochemical analysis combined with atmospheric environment analysis in actual service area. The results show that intergranular corrosion occurs mainly in aluminum alloy junction plates, and the corrosion products are mainly sulfides and chlorides of aluminum, and the corrosion potential of aluminum alloy junction plates is reduced by Cln- and sulfides in the atmosphere. The corrosion current density is increased, which is the main factor leading to corrosion failure of aluminum alloy junction board.
【作者單位】： 全球能源互聯(lián)網(wǎng)研究院;國網(wǎng)福建省電力有限公司泉州供電公司;國網(wǎng)福建省電力有限公司電力科學(xué)研究院;
【基金】：國家電網(wǎng)公司科技項(xiàng)目(5455DW170009)
【分類號(hào)】：TG178

【相似文獻(xiàn)】

相關(guān)期刊論文 前2條

1 黃豐;肖凱;李鵬云;聶銘;;變壓器接線板失效分析[J];鑄造技術(shù);2013年01期

2 姚明仁;;電石爐短網(wǎng)銅管與軟纜接線板連接方式的探討[J];電工技術(shù);2000年11期

，

本文編號(hào)：1904086