本文選題：金屬材料 + 超細晶TWIP鋼　； 參考：《材料研究學報》2017年11期

【摘要】：研究了不同退火溫度對大變形異步與同步復合冷軋制TWIP鋼(Fe-0.5C-18.6Mn-1.5Al-0.5Si)的組織和性能的影響,結果表明:經(jīng)96%大變形軋制后的材料組織明顯細化,抗拉強度從593 MPa提升至2021 MPa;在500℃以下退火,大變形軋制超細晶TWIP鋼未發(fā)生再結晶;在500~600℃發(fā)生部分再結晶;在600℃以上則發(fā)生完全再結晶。隨著退火溫度升高,材料強度降低,但塑性增加,大變形異步-同步軋制后經(jīng)700℃退火獲得了平均晶粒尺寸600 nm的超細晶TWIP鋼,并表現(xiàn)出優(yōu)秀的綜合力學性能,其強度、塑性分別達到1114 MPa、59.4%。此外,制備的TWIP鋼在500℃~600℃退火時,奧氏體基體中生成了大量細小彌散的硬質(zhì)DO3結構的(Fe,Mn)3(Al,Si)型金屬間化合物,顯著提高了材料強度。
[Abstract]:The effect of annealing temperature on the microstructure and properties of TWIP steel Fe-0.5C-18.6Mn-1.5Al-0.5Si) made by asynchronous and synchronous cold rolling with large deformation was studied. The results showed that the microstructure of TWIP steel rolled by 96% large deformation was refined obviously. The tensile strength was raised from 593 MPa to 2021 MPA, annealed below 500 鈩，