本文選題：Ni-P電刷鍍層 + 電接觸強(qiáng)化　； 參考：《熱加工工藝》2017年22期

【摘要】：在40Cr表面通過電刷鍍技術(shù)制備Ni-P鍍層,利用電接觸技術(shù)對該鍍層進(jìn)行強(qiáng)化。進(jìn)一步通過光學(xué)顯微鏡、掃描電鏡、能譜儀、X射線衍射分析和顯微硬度測試儀研究了鍍層強(qiáng)化前后的組織與性能。結(jié)果表明:通過電接觸強(qiáng)化技術(shù)制備了一種高性能冶金鍍層,鍍層缺陷較少,硬度達(dá)780.79 HV0.1。鍍層與基體的結(jié)合方式從機(jī)械結(jié)合變成冶金結(jié)合,鍍層中產(chǎn)生了新相Ni_3P。
[Abstract]:The Ni-P coating was prepared on the surface of 40Cr by brush plating, and the coating was strengthened by electric contact technique.The microstructure and properties of the coating before and after strengthening were studied by means of optical microscope, scanning electron microscope, X-ray diffraction analysis and microhardness tester.The results showed that a kind of high performance metallurgical coating was prepared by means of electrical contact strengthening technology. The defects of the coating were less and the hardness was up to 780.79 HV0.1.The bonding mode between coating and substrate changed from mechanical bonding to metallurgical bonding, and a new phase Ni3Pin was produced in the coating.
【作者單位】： 東華大學(xué)機(jī)械工程學(xué)院;
【基金】：上海市重點學(xué)科建設(shè)資助項目(B602)
【分類號】：TG174.44

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 向文才;;對電接觸爐有關(guān)公式的認(rèn)識[J];金屬制品;1989年03期

2 楚振斌;電接觸磨削實驗報告[J];機(jī)床與工具;1957年12期

3 趙志明;電接觸爐電壓公式的探討及對傳統(tǒng)公式的質(zhì)疑[J];金屬制品;1988年02期

4 趙志明;電接觸爐電壓公式中有關(guān)鋼絲預(yù)熱溫度的探討及計算[J];金屬制品;1990年01期

5 鐘玉川;;電接觸切割設(shè)備[J];機(jī)械設(shè)計與制造;1988年01期

6 朱振榮;新型電接觸薄膜保護(hù)劑的發(fā)展[J];宇航材料工藝;1987年05期

7 胡冀遠(yuǎn);蔡建國;;利用電接觸爐生產(chǎn)正火鋼絲[J];金屬制品;1991年05期

8 陳定一;居德明;;電接觸電阻加熱擠(滾)壓高鉻鑄鐵的實驗研究[J];安徽工學(xué)院學(xué)報;1989年01期

9 鐘燦賢;彈簧鋼件在水介質(zhì)中電接觸處理法[J];國外金屬熱處理;1997年01期

10 陳定一;電接觸電阻加熱擠壓鎳、鉻金合鑄鐵[J];機(jī)床;1987年02期

相關(guān)會議論文 前1條

1 于軍琪;孫龍杰;席愛民;;鋼絲電接觸運動加熱溫度的模糊神經(jīng)網(wǎng)絡(luò)控制[A];全國冶金企業(yè)計控網(wǎng)絡(luò)化研討會論文集[C];2003年

相關(guān)碩士學(xué)位論文 前3條

1 朱浩;42CrMo鋼表面涂層制備工藝的研究[D];東華大學(xué);2017年

2 郝曉磊;電接觸強(qiáng)化預(yù)涂層的制備[D];東華大學(xué);2017年

3 羅湘;高性能鎳基厚涂層的制備工藝及強(qiáng)化[D];東華大學(xué);2017年

，

本文編號：1750385