本文選題：鎳基合金 + 激光焊接�。� 參考：《焊接學報》2017年08期

【摘要】：Hastelloy X和Haynes 230分別是F級和G/H級燃燒室薄壁筒體用的鎳基高溫合金,采用光纖激光器對2mm厚度的兩類鎳基合金板材進行焊接試驗,并對比焊態(tài)及焊后固溶處理的接頭組織性能.結果表明,焊態(tài)Hastelloy X的焊縫中碳化物呈網(wǎng)絡狀析出,其硬度高、韌性差,固溶處理后出現(xiàn)柵狀組織及脆性Fe2W相.在焊縫一次枝晶內的枝晶生長方向線性排列,取向各異,熱影響區(qū)晶內也存在柵狀組織.Haynes 230晶粒較小,焊縫碳化物沿樹枝晶晶界鏈狀斷續(xù)析出,固溶處理后平直晶界變?yōu)閺澢Ы?蠕變性能得到提高.
[Abstract]:Hastelloy X and Haynes 230 are nickel based superalloys for thin wall cylinder of F and G / H combustors, respectively. Two kinds of nickel base alloy plates with 2mm thickness were welded by fiber laser, and the microstructure and properties of welded joints were compared.The results show that the carbides in welded Hastelloy X weld are network precipitated, with high hardness and poor toughness. After solution treatment, gate structure and brittle Fe2W phase appear.The dendritic growth direction in the primary dendrite of the weld is linear and the orientation is different. The grain size of the gate structure. Haynes 230 is smaller in the HAZ, and the weld carbide precipitates intermittently along the dendritic boundary.After the solution treatment, the straight grain boundary changes into the bending grain boundary, and the creep property is improved.
【作者單位】： 清華大學機械工程系;清華大學摩擦學國家重點實驗室;東方汽輪機有限公司工藝部;
【分類號】：TG456.7

【相似文獻】

相關期刊論文 前2條

1 劉冬梅;胡銳;李金山;劉毅;寇宏超;傅恒志;;Haynes 230合金在1100℃的恒溫氧化行為(英文)[J];稀有金屬材料與工程;2008年09期

2 姚燕生;王園園;李修宇;;激光復合焊接技術綜述[J];熱加工工藝;2014年09期

相關博士學位論文 前1條

1 王金鳳;DP1000雙相鋼激光焊接HAZ軟化及接頭性能研究[D];天津大學;2016年

相關碩士學位論文 前1條

1 孫明升;DP980高強鋼激光焊組織性能的研究[D];天津大學;2016年

，

本文編號：1738363