本文選題：低碳鑄鋼　切入點：亞溫淬火　出處：《材料熱處理學報》2017年03期

【摘要】：采用金屬模具澆注新型ZG20CrSiMn槽幫低碳耐磨鑄鋼,研究了亞溫淬火熱處理(QLT)和深冷處理(DCT)復合熱處理對其顯微組織、力學性能和耐磨損性能的影響。結果表明,與常規(guī)調質(QT)、QT+DCT及QLT工藝相比,復合熱處理(QLT+DCT)工藝可以顯著提高ZG20CrSiMn鋼的抗拉強度、韌性以及抗磨損性能。經(jīng)QLT+DCT工藝處理后的ZG20CrSiMn鋼,具有良好的抗拉強度及韌性,這與層片狀的細小回火索氏體組織和一定比例的鐵素體有關。與QT+DCT工藝處理樣品對比,QLT+DCT工藝處理樣品具有更好的耐磨損性能。
[Abstract]:A new type of low carbon wear-resistant cast steel with ZG20CrSiMn groove was cast by metal die. The effects of subtemperature quenching heat treatment (QT) and cryogenic treatment on microstructure, mechanical properties and wear resistance of the steel were studied. Compared with the conventional quenched and tempered QT / QT DCT and QLT processes, the composite heat treatment / QLTDCT process can significantly improve the tensile strength, toughness and wear resistance of the ZG20CrSiMn steel. The ZG20CrSiMn steel treated by the QLT DCT process has good tensile strength and toughness. These results are related to the microstructure of fine tempering solids and a certain proportion of ferrite. Compared with the samples treated by QT DCT process, the samples treated by QLT DCT process have better wear resistance.
【作者單位】： 山西工程技術學院;太原理工大學材料科學與工程學院;太原科技大學材料科學與工程學院;
【基金】：2014年度山西省煤基重點科技攻關項目(MC2014-02) 太原科技大學校博士科研啟動項目(20152011)
【分類號】：TG142.1;TG161

【相似文獻】

相關期刊論文 前10條

1 王云霖;閂體的復合熱處理[J];兵器材料科學與工程;1985年04期

2 高彩橋,靳忠效;復合熱處理[J];機械工程師;1986年01期

3 梁淑榮,李新生;精密冷擠零件的復合熱處理工藝[J];金屬熱處理;2000年08期

4 李新生,梁淑榮;精密冷擠零件的復合熱處理工藝[J];機械工藝師;2001年01期

5 蔣寧;;復合熱處理工藝與節(jié)能環(huán)保良性互動[J];重慶三峽學院學報;2009年03期

6 高彩橋;復合熱處理與復合化學熱處理[J];固體潤滑;1986年02期

7 鮒田清司;易泓可;;復合熱處理動向[J];國外金屬熱處理;1986年01期

8 何則榮;蔡傳榮;;40Cr鋼復合熱處理強韌化[J];金屬科學與工藝;1987年03期

9 何則榮;鋼復合熱處理強韌化的研究[J];福州大學學報(自然科學版);1988年03期

10 林吉清;針板新工藝—多工序相變復合熱處理[J];機械設計與研究;1991年03期

相關碩士學位論文 前1條

1 謝仔新;基于GM標準的高強度汽車緊固件復合熱處理生產(chǎn)技術研究[D];浙江工業(yè)大學;2013年

，

本文編號：1672829