【摘要】：采用表面分析和電化學(xué)手段研究了靜態(tài)磁場(chǎng)對(duì)硫酸鹽還原菌(SRB)在304不銹鋼表面吸附性能的影響。結(jié)果表明:磁場(chǎng)強(qiáng)度為150 mT對(duì)浮游SRB的生長(zhǎng)沒(méi)有明顯的影響,但是可以延遲固著SRB的形成;靜態(tài)磁場(chǎng)可以抑制SRB生物膜在304不銹鋼表面的形成和吸附,磁場(chǎng)強(qiáng)度為4 mT時(shí)比150 mT時(shí)的效果更好。使用X射線(xiàn)光電子能譜(XPS)對(duì)腐蝕產(chǎn)物進(jìn)行分析表明,在靜態(tài)磁場(chǎng)條件下腐蝕產(chǎn)物中有鐵氧化物生成。
[Abstract]:The effect of static magnetic field on the adsorption properties of sulfate-reducing bacteria SRB on 304 stainless steel was studied by surface analysis and electrochemical methods. The results showed that the magnetic field intensity of 150mT had no obvious effect on the growth of SRB. The static magnetic field can inhibit the formation and adsorption of SRB biofilm on the surface of 304 stainless steel. When the magnetic field intensity is 4 Mt, the effect is better than that at 150 Mt. The analysis of corrosion products by X-ray photoelectron spectroscopy (XPS) shows that iron oxides are formed in the corrosion products under static magnetic field.
【作者單位】： 華中科技大學(xué)化學(xué)與化工學(xué)院材料服役與失效湖北省重點(diǎn)實(shí)驗(yàn)室;深圳華中科技大學(xué)研究院;海軍工程大學(xué)理學(xué)院;
【基金】：國(guó)家自然科學(xué)基金項(xiàng)目(51171067) 深圳市基礎(chǔ)研發(fā)基金項(xiàng)目(JC201005310696A) 華中科技大學(xué)創(chuàng)新基金項(xiàng)目(國(guó)合專(zhuān)項(xiàng)2015ZZGH010,前沿探索類(lèi)2015TS150) 材料化學(xué)與服役失效湖北省重點(diǎn)實(shí)驗(yàn)室基金項(xiàng)目(201502)資助
【分類(lèi)號(hào)】：TG142.71;TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 李林;;油田生產(chǎn)中硫酸鹽還原菌的危害及其防治[J];化工時(shí)刊;2010年09期

2 N.N.Lyalikova;裘榮慶;;應(yīng)用硫酸鹽還原菌富集礦石[J];國(guó)外金屬礦選礦;1979年07期

3 劉魁元;;硫酸鹽還原菌抑制劑的研究與應(yīng)用概況[J];工業(yè)水處理;1984年04期

4 李文融;硫酸鹽還原菌[J];工業(yè)水處理;1986年01期

5 李凡修;;預(yù)防石油開(kāi)采中硫酸鹽還原菌生長(zhǎng)的抑制劑[J];鉆采工藝;1990年03期

6 師祥洪;;淺談?dòng)吞镒⑺到y(tǒng)中硫酸鹽還原菌的取樣方法[J];油氣田環(huán)境保護(hù);1992年04期

7 劉宏芳,黃茁,許立銘,鄭家q，

本文編號(hào)：1632089