本文選題：TA鈦合金　切入點(diǎn)：β鍛　出處：《Transactions of Nonferrous Metals Society of China》2017年11期 　論文類型：期刊論文

【摘要】：為了研究在β鍛TA15兩相鈦合金中的變形帶,在Gleeble 3500熱模擬實(shí)驗(yàn)機(jī)上進(jìn)行熱模擬壓縮試驗(yàn),同時(shí)通過光學(xué)顯微鏡(OM)和電子背散射衍射(EBSD)對顯微組織進(jìn)行研究。研究發(fā)現(xiàn):在TA15鈦合金β變形中,變形帶在溫度高達(dá)0.7T_m(T_m為熔點(diǎn))時(shí)仍是重要的組織細(xì)化機(jī)制。變形帶的邊界可以是尖銳或者連續(xù)變化的。尖銳的變形帶界面能夠阻礙不連續(xù)動(dòng)態(tài)再結(jié)晶形核,從而抑制再結(jié)晶的發(fā)生,而連續(xù)變化的界面是連續(xù)動(dòng)態(tài)再結(jié)晶產(chǎn)生之處。變形帶在高應(yīng)變速率和初始粗晶組織中更加明顯。分裂后的晶粒寬度對應(yīng)變速率敏感,但受溫度和初始晶粒尺寸影響較小。多向鍛造產(chǎn)生交織的變形帶可用于細(xì)化小型鍛件的組織。
[Abstract]:In order to study the deformation band in 尾 -forged TA15 two-phase titanium alloy, a thermal simulation compression test was carried out on a Gleeble 3500 thermal simulator. At the same time, the microstructure of TA15 titanium alloy was studied by optical microscope and electron backscatter diffraction (EBSD). Deformation zone is still an important mechanism of microstructure refinement when temperature is up to 0.7 T / m). The boundary of deformation zone can be sharp or continuous. Sharp deformation band interface can hinder dynamic recrystallization nucleation. Thus the occurrence of recrystallization is inhibited, and the continuously changing interface is where the continuous dynamic recrystallization occurs. The deformation zone is more obvious in the high strain rate and initial coarse grain structure. The grain width after splitting is sensitive to the strain rate. However, the effect of temperature and initial grain size is small. The interwoven deformation band produced by multi-direction forging can be used to refine the microstructure of small forgings.
【作者單位】： 西北工業(yè)大學(xué)材料學(xué)院凝固技術(shù)國家重點(diǎn)實(shí)驗(yàn)室;
【基金】：Projects(51205317,51575449)supported by the National Natural Science Foundation of China;Project(50935007)supported by the National Natural Science Foundation of China for Key Program Project(3102015AX004)supported by the Fundamental Research Funds for the Central Universities,China Project(104-QP-2014)supported by the Research Fund of the State Key Laboratory of Solidification Processing,China
【分類號(hào)】：TG146.23

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 江慧豐,張青川,蔣震宇,趙思敏,陳忠家,伍小平;鋁合金中PLC變形帶的軌跡觀察和研究[J];實(shí)驗(yàn)力學(xué);2004年04期

2 楊續(xù)躍;姜育培;;鎂合金熱變形下變形帶的形貌和晶體學(xué)特征[J];金屬學(xué)報(bào);2010年04期

3 劉勇;朱景川;王洋;;TA15合金熱擠壓過程中晶界特征分布研究[J];材料熱處理學(xué)報(bào);2009年02期

4 劉瑞民,李興無,沙愛學(xué);TA15合金板材的組織和性能研究[J];材料開發(fā)與應(yīng)用;2005年04期

5 王斌;郭鴻鎮(zhèn);姚澤坤;趙靜;趙張龍;張明淵;;復(fù)合形變熱處理對TA15近α鈦合金組織和性能的影響[J];材料熱處理學(xué)報(bào);2006年05期

6 李行志;胡樹兵;肖建中;籍龍波;;組織不均勻性對TA15電子束焊接接頭疲勞裂紋擴(kuò)展的影響[J];中國有色金屬學(xué)報(bào);2010年12期

7 許海鷹;張偉;曹子文;車志剛;鄒世坤;;激光沖擊強(qiáng)化優(yōu)化TA15電子束焊接接頭的組織性能(英文)[J];稀有金屬材料與工程;2013年S2期

8 韓冠軍;楊合;樊曉光;孫念光;;TA15合金大型筋板件等溫局部加載晶粒尺寸演化研究[J];塑性工程學(xué)報(bào);2009年05期

9 王向明,劉文s，

本文編號(hào)：1606403