本文選題：雙螺桿擠出機(jī)　切入點(diǎn)：疲勞斷裂　出處：《機(jī)械工程材料》2017年03期 　論文類型：期刊論文

【摘要】：某雙螺桿擠出機(jī)的螺桿在運(yùn)行過程中發(fā)生早期斷裂,通過斷口的宏觀觀察和掃描電鏡觀察、化學(xué)成分分析、顯微組織觀察、力學(xué)性能測試和有限元模擬,找出了螺桿軸斷裂失效的原因。結(jié)果表明:螺桿軸發(fā)生了扭轉(zhuǎn)疲勞斷裂,裂紋起源于齒根,且有多個(gè)疲勞源;芯軸的花鍵齒根部是螺桿軸應(yīng)力集中的部位;熱處理工藝欠佳導(dǎo)致材料內(nèi)部微孔聚集、組織不均勻,這些因素最終致使螺桿軸發(fā)生早期疲勞斷裂。
[Abstract]:The screw of a twin-screw extruder had an early fracture in the course of operation. Through macroscopic observation of fracture surface, SEM observation, chemical composition analysis, microstructure observation, mechanical property test and finite element simulation, The results show that torsional fatigue fracture occurs in the screw shaft, the crack originates from the root of the tooth and there are many fatigue sources, and the spline tooth root of the core shaft is the part of the stress concentration of the screw shaft. The poor heat treatment process leads to the accumulation of micropores and uneven microstructure, which leads to the early fatigue fracture of the screw shaft.
【作者單位】： 華南理工大學(xué)機(jī)械與汽車工程學(xué)院;
【分類號】：TG115

【參考文獻(xiàn)】

相關(guān)期刊論文 前4條

1 馬小明;黃志華;;聚丙烯擠出機(jī)螺桿軸斷裂失效分析[J];機(jī)械工程材料;2014年10期

2 袁衛(wèi)明;傅紀(jì)國;;注塑機(jī)螺桿強(qiáng)度的分析計(jì)算[J];輕工機(jī)械;2012年02期

3 劉陽春;鋁型材擠壓模的選材及其熱處理[J];國外金屬熱處理;2001年05期

4 陳煜國,李相麟,扶名福;微孔洞型的分形斷裂理論初探[J];應(yīng)用力學(xué)學(xué)報(bào);1998年04期

相關(guān)碩士學(xué)位論文 前2條

1 謝兆興;高扭矩深槽嚙合同向雙螺桿設(shè)計(jì)及受力分析[D];北京化工大學(xué);2011年

2 王申存;低碳低合金滲碳鋼的組織、性能與晶體學(xué)特征的研究[D];中南大學(xué);2010年

【共引文獻(xiàn)】

相關(guān)期刊論文 前6條

1 馬小明;周陽;;高速雙螺桿擠出機(jī)螺桿軸斷裂失效分析[J];機(jī)械工程材料;2017年03期

2 郭奕文;鄧運(yùn)來;王宇;劉勝膽;;2024鋁合金航空座椅支承零件等溫模鍛成形研究[J];鍛壓技術(shù);2016年08期

3 馬小明;肖鵬;;38CrMoAlA擠出機(jī)螺桿軸斷裂失效分析[J];熱加工工藝;2016年10期

4 馬小明;黃志華;;聚丙烯擠出機(jī)螺桿軸斷裂失效分析[J];機(jī)械工程材料;2014年10期

5 王紅斌;劉海燕;;分形理論在有機(jī)玻璃有效彈性模量及裂紋聚合路徑研究中的應(yīng)用[J];玻璃;2014年06期

6 郭雋,郭成璧;高溫疲勞表面短裂紋的分形研究[J];固體力學(xué)學(xué)報(bào);2002年02期

【二級參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 楊s，

本文編號：1567838