本文選題：熱作模具鋼　切入點(diǎn)：初生碳氮化物　出處：《工程科學(xué)學(xué)報(bào)》2017年01期 　論文類型：期刊論文

【摘要】：實(shí)驗(yàn)證明H13鋼中存在三類初生碳氮化物,包括富V和C的(V_x,Mo_(1-x))(C_y,N_(1-y))、富Ti和N的(Ti_x,V_(1-x))(C_y,N_(1-y))及富V和C的(Ti_x,V_(1-x))(C_y,N_(1-y)),部分存在形核核心.基于雙亞點(diǎn)陣模型和凝固偏析模型分析計(jì)算H13鋼凝固過(guò)程中元素含量變化,考慮初生碳氮化物中元素間的相互作用,根據(jù)三類碳氮化物中合金元素含量和C/N比值不同,對(duì)各碳氮化物的生成自由能進(jìn)行分析.理論研究指出富Ti和N的(Ti_x,V_(1-x))(C_y,N_(1-y))在固相率為0.90時(shí)即可生成,而富V和C的(Ti_x,V_(1-x))(C_y,N_(1-y))在固相率大于0.96才可生成,兩類碳氮化物的臨界生成固相率fP均隨固溶Ti和N含量的增加而減小.(V_x,Mo_(1-x))(C_y,N_(1-y))的臨界生成固相率與x值密切相關(guān),x減小時(shí)fP降低,粒子尺寸增加,實(shí)驗(yàn)與理論分析吻合良好.根據(jù)錯(cuò)配度分析氧化物和碳氮化物對(duì)H13鋼中初生碳氮化物異質(zhì)形核的作用.
[Abstract]:The experimental results show that there are three kinds of primary carbonitride in H13 steel. Including the V / V / C / V / S / V / S / V / C / V / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / V / C / C / C / C / C / C / C / C / C / V / C / C / V / C / C / V / C / C / C / C / V / C / C / V / C / C / V / C / C / V / S / V / C / C / C / C / V / C / C / C / V / C / C / C / C / C / C / C / V / C. Considering the interaction between elements in primary carbonitride, according to the content of alloy elements and the ratio of C / N in three kinds of carbonitride, The free energy of formation of each carbon nitride is analyzed. The theoretical study indicates that the TixV / T / T / T / T / T / T / T / T / T / T / T / T / T / T / T / T / T / T / C / T / T / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C / C /. The critical solid state fraction (FP) of the two carbonitride compounds decreases with the increase of Ti and N contents. The critical solid state rate of the two kinds of carbonitride compounds decreases with the increase of Ti and N contents. The critical solid state rate of the two kinds of carbonitride compounds is closely related to the value of x, and the particle size increases, and the critical solid rate decreases with the increase of Ti and N contents. According to the mismatch, the effect of oxide and carbonitride on the heterogenetic nucleation of primary carbon nitride in H13 steel was analyzed.
【作者單位】： 北京科技大學(xué)冶金與生態(tài)工程學(xué)院;鋼鐵研究總院高溫材料研究所;
【分類號(hào)】：TG142.1

【相似文獻(xiàn)】

相關(guān)會(huì)議論文 前5條

1 潘紅;曾建華;吳國(guó)榮;;釩鈦鋼中碳氮化物的析出熱力學(xué)計(jì)算[A];2013釩鈦高強(qiáng)鋼開(kāi)發(fā)與應(yīng)用技術(shù)交流會(huì)論文集[C];2013年

2 汪春雷;趙和明;;影響鋼中鈮的碳氮化物固溶的因素分析[A];中國(guó)金屬學(xué)會(huì)特鋼分會(huì)，特鋼冶煉學(xué)術(shù)委員會(huì)2009年會(huì)論文集[C];2009年

3 徐溫崇;孫福玉;趙佩祥;;(Nb、V)碳氮化物在鋼中應(yīng)變誘導(dǎo)析出動(dòng)力學(xué)[A];第四次全國(guó)電子顯微學(xué)會(huì)議論文摘要集[C];1986年

4 婁艷芝;柏明卓;倪曉青;柳得櫓;;CSP工藝生產(chǎn)微鈦鋼中的碳氮化物析出相[A];2005年全國(guó)電子顯微學(xué)會(huì)議論文集[C];2005年

5 程四華;周玉麗;邸全康;王勇;王立峰;;基于超快冷工藝的高強(qiáng)精軋螺紋鋼中碳氮化物析出[A];線棒材工藝技術(shù)、裝備與應(yīng)用學(xué)術(shù)研討會(huì)論文集[C];2012年

相關(guān)博士學(xué)位論文 前2條

1 曹建春;鈮鉬復(fù)合微合金鋼中碳氮化物沉淀析出研究[D];昆明理工大學(xué);2006年

2 周燦棟;高氮35CrMoV鋼的制備和研究[D];上海大學(xué);2001年

相關(guān)碩士學(xué)位論文 前3條

1 賈鈺澤;高氮馬氏體不銹軸承鋼的碳氮化物演變與強(qiáng)韌性能的研究[D];昆明理工大學(xué);2015年

2 張明;含釩鋼中析出粒子對(duì)組織超細(xì)化的影響研究[D];江蘇大學(xué);2007年

3 王雙寶;T92鍋爐鋼抗高溫性能及其微觀組織表征[D];湖南大學(xué);2009年

，

本文編號(hào)：1557096