【摘要】：本研究以水泥、礦渣粉煤灰為固化劑,通過使用硫酸鹽和氫氧化鈉來激發(fā)礦渣、粉煤灰改性疏浚淤泥,按照控制變量的方法設(shè)計(jì)兩種激發(fā)劑占淤泥含量的不同比例,進(jìn)行固化然后抗剪試驗(yàn),得出在各種配比下的c、φ值。比較兩種激發(fā)劑激發(fā)礦渣粉煤灰對(duì)淤泥改性后的抗剪強(qiáng)度影響。發(fā)現(xiàn)在堿性環(huán)境下粉煤灰和礦渣的激發(fā)效果更好,改性后的淤泥各項(xiàng)指標(biāo)均有所提高。以期為提高疏浚淤泥利用率提供一條途徑。
[Abstract]:In this study, cement and slag fly ash were used as curing agents to activate slag by using sulfate and sodium hydroxide. Fly ash was used to modify dredged silt. According to the method of controlling variables, two activators were designed to account for different proportion of sludge content. The solidification and shear resistance tests were carried out, and the c, 蠁 values were obtained under various ratios. The effects of activated slag and fly ash on the shear strength of silt modified by two activators were compared. It was found that the activation effect of fly ash and slag was better in alkaline environment, and the indexes of modified sludge were improved. It is expected to provide a way to improve the utilization ratio of dredged silt.
【作者單位】： 連云港市市區(qū)水工程管理處;
【分類號(hào)】：X703;TU52

【相似文獻(xiàn)】

相關(guān)期刊論文 前3條

1 鄧統(tǒng)輝;褚技威;曹永軍;;某尾礦料的抗剪試驗(yàn)研究[J];西部探礦工程;2011年02期

2 徐有鄰,邸小壇,劉立新,向忠,錢偉;玻璃纖維水泥砂漿墻體加固抗剪試驗(yàn)研究[J];建筑科學(xué);1999年02期

3 ;[J];;年期

相關(guān)會(huì)議論文 前3條

1 宋克強(qiáng);;巖石軟弱結(jié)構(gòu)面抗剪強(qiáng)度的研究——單一試件的抗剪試驗(yàn)的指標(biāo)分析[A];地下工程經(jīng)驗(yàn)交流會(huì)論文選集[C];1982年

2 繆升;雷鴻君;;配筋混凝土空心小砌塊墻體抗剪試驗(yàn)擬合研究[A];第二屆全國(guó)防震減災(zāi)工程學(xué)術(shù)研討會(huì)論文集[C];2005年

3 鮑從桂;;穿條式鋁合金隔熱型材抗剪力影響因素的分析[A];2013年全國(guó)鋁加工技術(shù)及應(yīng)用交流會(huì)論文集[C];2013年

，

本文編號(hào)：2272274