【摘要】：氯離子滲透是導(dǎo)致鋼筋混凝土結(jié)構(gòu)耐久性能退化的重要原因之一。荷載作用會對混凝土的孔隙和裂縫產(chǎn)生影響,改變混凝土抗氯離子侵蝕的能力,加速混凝土結(jié)構(gòu)的耐久性退化。目前對靜力荷載作用下氯離子在混凝土中的擴散行為開展了一定研究,但對疲勞荷載下混凝土中氯離子的滲透性能研究較少。該文總結(jié)了近年來國內(nèi)外文獻報道中關(guān)于疲勞荷載作用下氯離子在混凝土中傳輸行為的研究成果,包括試驗方法、擴散行為、擴散機理、影響因素以及擴散模型等,并對現(xiàn)階段研究工作存在的不足提出了建議。
[Abstract]:Chloride ion permeation is one of the important reasons for durability degradation of reinforced concrete structures. The loading will affect the pore and crack of concrete, change the ability of resisting chloride ion erosion of concrete, and accelerate the durability degradation of concrete structure. At present, the diffusion behavior of chloride ions in concrete under static load has been studied, but the permeability of chloride ions in concrete under fatigue load is less studied. This paper summarizes the research results of chloride ion transport in concrete under fatigue load reported in recent years, including test method, diffusion behavior, diffusion mechanism, influencing factors and diffusion model, etc. At the same time, some suggestions are put forward for the deficiency of the present research work.
【作者單位】： 長沙理工大學(xué)土木與建筑學(xué)院;武漢新港投國際集裝箱有限公司;南方地區(qū)橋梁長期性能提升技術(shù)國家地方聯(lián)合工程實驗室;
【基金】：國家重點基礎(chǔ)研究發(fā)展計劃(973計劃)資助項目(編號:2015CB057701) 國家自然科學(xué)基金資助項目(編號:51578078) 湖南省教育廳科學(xué)研究重點項目(編號:14A005);湖南省教育廳青年項目(編號:06C044)
【分類號】：TU528

【相似文獻】

相關(guān)期刊論文 前1條

1 王余富;;疲勞荷載權(quán)函數(shù)下混凝土疲勞累積損傷值的研究[J];固體力學(xué)學(xué)報;2010年S1期

相關(guān)會議論文 前1條

1 唐先習(xí);梁金寶;唐先周;徐岳;;疲勞荷載作用下受壓混凝土應(yīng)變性能試驗研究[A];第22屆全國結(jié)構(gòu)工程學(xué)術(shù)會議論文集第Ⅱ冊[C];2013年

相關(guān)碩士學(xué)位論文 前1條

1 孫美麗;多級等幅疲勞荷載作用下RPC的疲勞累積損傷研究[D];北京交通大學(xué);2009年

，

本文編號：2185130