本文選題：Ni-SiC + 納米鍍層�。� 參考：《功能材料》2017年09期

【摘要】：采用超聲波輔助電沉積方式,在45鋼表面制備了Ni-SiC納米復(fù)合鍍層。根據(jù)陰極電流密度、PH值和攪拌速度對(duì)Ni-SiC納米復(fù)合鍍層SiC粒子復(fù)合量的影響,獲取Ni-SiC納米復(fù)合鍍層最佳條件的工藝參數(shù);并利用掃描電鏡(SEM)、高分辨率透射電鏡(HRTEM)研究工藝參數(shù)對(duì)Ni-SiC納米復(fù)合鍍層表面形貌和微觀組織結(jié)構(gòu)的影響。結(jié)果表明,獲取Ni-SiC納米復(fù)合鍍層最佳工藝參數(shù)為陰極電流密度6A/dm~2,pH值=4,攪拌速度300r/min。由最佳工藝參數(shù)制得的Ni-SiC納米復(fù)合鍍層表面呈胞狀,SiC粒子粒徑尺寸較小,其平均粒徑為21.5nm。
[Abstract]:Ni-SiC nanocomposite coating was prepared on 45 steel surface by ultrasonic assisted electrodeposition.According to the effect of cathodic current density and stirring speed on the amount of Ni-SiC nano-composite coating SiC particles, the optimum process parameters of Ni-SiC nano-composite coating were obtained.The effects of process parameters on the surface morphology and microstructure of Ni-SiC nanocomposite coatings were studied by SEM and HRTEM.The results show that the optimal process parameters for obtaining Ni-SiC nanocomposite coating are cathode current density of 6A / dmm2p4 and stirring speed of 300r-1 路min.The average particle size of Ni-SiC nano-composite coating was 21.5 nm.
【作者單位】： 東北石油大學(xué)機(jī)械科學(xué)與工程學(xué)院;川慶鉆探公司長(zhǎng)慶石油工程監(jiān)督公司;
【基金】：國(guó)家自然科學(xué)基金資助項(xiàng)目(51474072)
【分類號(hào)】：TQ153

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 王平;程英亮;張昭;;不同的SiC納米顆粒鍍前處理對(duì)Ni-SiC納米復(fù)合鍍層性能的影響[J];材料保護(hù);2010年11期

2 譚澄宇;劉宇;胡煒;崔航;;Ni-SiC電結(jié)晶沉積層的阻抗譜及SiC顆粒對(duì)Ni沉積的影響[J];材料保護(hù);2009年05期

3 陳麗莉;;基于BP模型的Ni-SiC鍍層鍍速預(yù)測(cè)研究[J];兵器材料科學(xué)與工程;2014年03期

4 張文峰;;基于電鑄技術(shù)制備Ni-SiC復(fù)合材料的組織及斷口特征[J];人工晶體學(xué)報(bào);2008年06期

，

本文編號(hào)：1761760