本文選題：氧化錳尾礦　切入點(diǎn)：SO　出處：《有色金屬(冶煉部分)》2017年05期 　論文類型：期刊論文

【摘要】：在硫酸溶液中,以SO_2為還原劑對(duì)氧化錳尾礦進(jìn)行還原浸出,浸出液凈化后與碳酸氫銨發(fā)生沉淀反應(yīng)回收碳酸錳。在最優(yōu)浸出條件下,錳浸出率達(dá)96%以上。采用氨水調(diào)節(jié)pH為5.2時(shí),浸出液中的鐵、鋁、硅的去除率分別為100%、99.6%和96.9%。凈化液與碳酸氫銨反應(yīng)沉淀率為99.8%,整個(gè)工藝錳回收率為90.5%,碳酸錳產(chǎn)品達(dá)到《HG/T4203-2011工業(yè)碳酸錳》一等品指標(biāo)要求。
[Abstract]:In sulfuric acid solution, manganese oxide tailings were leached with SO_2 as reducing agent. After purification, precipitation reaction occurred with ammonium bicarbonate to recover manganese carbonate. The leaching rate of manganese is more than 96%. When the pH value of ammonia is adjusted to 5. 2, the iron and aluminum in the leachate can be obtained. The removal rates of silicon were 99.6% and 96.9%, respectively. The precipitation rate of the purified solution reacted with ammonium bicarbonate was 99.8. The recovery rate of manganese carbonate in the whole process was 90.5%, and the manganese carbonate product reached the requirement of the first grade of manganese carbonate in HG/T4203-2011 industry.
【作者單位】： 鄭州職業(yè)技術(shù)學(xué)院電氣系;中國地質(zhì)科學(xué)院鄭州礦產(chǎn)綜合利用研究所;
【基金】：國土資源公益性行業(yè)科研專項(xiàng)(201211069)
【分類號(hào)】：TD926.4;TQ137.12

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 袁明亮,邱冠周;高純微晶碳酸錳制備中的粒度和質(zhì)量控制[J];中南工業(yè)大學(xué)學(xué)報(bào)(自然科學(xué)版);2001年05期

2 宋士強(qiáng);;大表面積二氧化錳的制造方法[J];無機(jī)鹽工業(yè);1980年05期

3 章淑軒;;碳酸錳制備的方法研究[J];化學(xué)工程與裝備;1985年01期

4 潘萬成;高純碳酸錳的制造方法[J];湖南化工;1989年01期

5 李緒福;;高純微晶狀碳酸錳的研制[J];無機(jī)鹽工業(yè);1991年04期

6 孟明權(quán),李春英,桑兆昌,賈林平;利用氫醌含錳廢渣制取碳酸錳[J];無機(jī)鹽工業(yè);1994年03期

7 陳書閣;碳酸錳分解氧化工藝條件的探討[J];無機(jī)鹽工業(yè);1994年06期

8 鐘國清,蔣禮;高純碳酸錳的制備研究[J];無機(jī)鹽工業(yè);1996年06期

9 胡修權(quán);孫猛;李桂玲;曹海華;賀愛平;周毅;;超微細(xì)碳酸錳合成影響因素控制[J];無機(jī)鹽工業(yè);2014年01期

10 趙立新,孫來九,郭人民,張小燕,孫寶蓮;含錳廢水制備高純碳酸錳除鈣的研究[J];無機(jī)鹽工業(yè);2001年06期

相關(guān)碩士學(xué)位論文 前2條

1 王俊紅;亞微米級(jí)碳酸錳和磷酸錳的制備研究[D];南昌大學(xué);2013年

2 李燕靈;高鐵菱錳礦制取高純碳酸錳的實(shí)驗(yàn)研究[D];貴州大學(xué);2014年

，

本文編號(hào)：1603751