本文選題：硝酸　切入點：焊縫　出處：《腐蝕與防護(hù)》2017年05期 　論文類型：期刊論文

【摘要】：通過化學(xué)成分分析、掃描電鏡觀察、能譜分析等方法,研究了硝酸管道焊縫腐蝕失效的原因。結(jié)果表明:304不銹鋼硝酸管道在焊縫的腐蝕失效主要發(fā)生在焊縫熱影響區(qū),出現(xiàn)晶間腐蝕,沿?zé)嵊绊憛^(qū)出現(xiàn)刀口狀腐蝕溝槽。三通母材的含碳量高于標(biāo)準(zhǔn)值,導(dǎo)致三通側(cè)的管材在焊接過程中,其熱影響區(qū)更容易發(fā)生敏化,晶粒粗大,導(dǎo)致耐蝕性下降。碳含量是影響304不銹鋼焊接接頭在硝酸中耐蝕性的關(guān)鍵因素,碳含量越高,焊接過程中熱影響區(qū)的不銹鋼越容易發(fā)生敏化,導(dǎo)致其耐蝕性顯著降低。
[Abstract]:By means of chemical composition analysis, scanning electron microscope observation and energy dispersive analysis, the causes of corrosion failure of nitric acid pipe weld are studied. The results show that the corrosion failure of the stainless steel nitric acid pipe in the weld mainly occurs in the heat-affected zone of the weld. The carbon content of the base metal is higher than the standard value, which results in the heat affected zone is more sensitive and the grain size is coarse during the welding process of the tube. Carbon content is the key factor that affects corrosion resistance of 304 stainless steel welded joint in nitric acid. The higher the carbon content, the easier sensitization of stainless steel in heat affected zone during welding process, which results in a significant decrease in corrosion resistance of 304 stainless steel welded joint.
【作者單位】： 北京化工大學(xué);中國石油吉林石化公司檢測中心;
【基金】：北京市與中央高校共建項目
【分類號】：TG457.11;TQ111.2

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 ;焊縫多次返修試驗[J];化工與通用機械;1976年07期

2 K.E.Dorschu;;受壓容器用鋼焊縫金屬的性能(續(xù))[J];化工與通用機械;1979年06期

3 徐堅,肖延齡,金月琴,谷其發(fā);催化分餾塔下段焊縫周圍母材的腐蝕[J];石油化工設(shè)備;1987年03期

4 ;國外焊接、焊縫檢驗、消除應(yīng)力等近況[J];化工煉油機械通訊;1972年02期

5 倪受剛;;2(1/4)Cr-1Mo焊縫金屬回火脆性的預(yù)防[J];化工與通用機械;1983年07期

6 K.Agusa;M.Kosho;N.Nishiyama;王德慶;;9Ni鋼的匹配鐵素體填料金屬焊條惰性氣體保護(hù)焊[J];低溫與特氣;1985年01期

7 K.E.Dorschu;陳裕川;;受壓容器用鋼焊縫金屬的性能(續(xù)二)[J];化工與通用機械;1979年07期

8 孟廣U，

本文編號：1559216