本文關鍵詞： 干燥收縮 減縮劑 水泥石 相對濕度 孔結(jié)構(gòu)　出處：《重慶大學》2015年碩士論文　論文類型：學位論文

【摘要】：本論文通過碟片法測試了水泥石在梯度濕度干燥條件下的干燥收縮與質(zhì)量損失,分析了減縮劑的不同使用方法(內(nèi)摻,外刷和浸泡)、摻量、品種等對水泥石干縮的影響。通過分析減縮劑對水溶液和Ca(OH)2溶液表面張力、水分蒸發(fā)速率、水泥石孔結(jié)構(gòu)等的影響規(guī)律,揭示了減縮劑的濕度分段減縮機理。與此同時,對減縮劑在不同水灰比(0.3、0.4、0.5),相對濕度(100%RH~12%RH),齡期(7d、28d、56d)等條件下的減縮效果及其與高效減水劑的相容性進行評價,確定了減縮劑的有效作用條件。另外,還試驗測定了減縮劑對水泥石的抗壓強度的影響。研究結(jié)果表明,對于早齡期(7d)的水泥石,減縮劑內(nèi)摻可以顯著減小水泥石的干燥收縮,SBT-SRA對0.3水灰比水泥石的減縮率為47.15%,減縮劑外刷和浸泡的方法對水泥石的減縮效果不明顯,最大的減縮率分別只有6.64%和8.27%;對于養(yǎng)護后期(56d)的水泥石來說,減縮劑的內(nèi)摻和浸泡水泥石的方法均起到顯著的減縮作用,最大的減縮率分別為45.53%和30.88%。減縮劑外刷的減縮效果較差,減縮率只有15.72%。減縮劑內(nèi)摻會降低水泥石的抗壓強度,且摻量越大,降低作用越明顯。當SBT-SRA的摻量為0.2%時,0.4水灰比的水泥石28d抗壓強度只有基準的84.5%;減縮劑以外刷或浸泡的方法使用時,對水泥石的強度有不同程度的提高,相同條件下水泥石28d抗壓強度都比基準組略高。在減縮機理方面,減縮劑內(nèi)摻大幅度降低孔溶液的表面張力是其減縮的最主要原因,同時減縮劑也通過降低孔溶液的蒸發(fā)速率(低濕度區(qū))來達到減縮的目的;使用減縮劑細化了水泥石的孔結(jié)構(gòu),使有害孔的數(shù)量減少,從而減小水泥石的干燥收縮。減縮劑內(nèi)摻時增大水泥石的總孔隙率,外刷和浸泡時則減小水泥石的總孔隙率,三種使用方法均對水泥石孔結(jié)構(gòu)起到細化作用。不同濕度條件下,減縮劑的減縮機理不同:在高濕度區(qū)(85%RH,75%RH和55%RH),減縮劑主要以減小孔溶液表面張力,從而減小水分蒸發(fā)引起的收縮應力來達到減縮目的;在低濕度區(qū)(25%RH和12%RH),減縮劑則主要以減少水泥石中孔溶液蒸發(fā)速率的機制來減小由于毛細水蒸發(fā)引起的總的收縮應力,從而起到減小干縮的作用。當GRA-SRA與聚羧酸高效減水劑復摻時,在100%RH~85%RH濕度段,與基準組相比28d水泥石出現(xiàn)了一定程度的膨脹,在55%RH~12%RH濕度段,GRA-SRA與聚羧酸高效減水劑復摻起到了一定的減縮效果,但不如GRA-SRA單摻時的減縮效果好,可見聚羧酸高效減水劑對GRA-SRA的減縮具有一定的負面作用。通過對幾乎涵蓋全濕度范圍的減縮劑的機理研究及其在不同作用條件下的減縮效果的評價,本論文對減縮劑產(chǎn)品的研發(fā)及其在實際工程中的推廣應用都有較高的理論指導意義。
[Abstract]:In this paper, the drying shrinkage and mass loss of cement stone under the condition of gradient humidity drying were measured by disc method, and the different use methods of shrinkage reducer (mixing, brushing and soaking) were analyzed. By analyzing the influence of shrinkage reducer on surface tension, evaporation rate and pore structure of water solution and Ca(OH)2 solution. At the same time, at the same time, the shrinkage reducer with different water / cement ratio of 0.3U 0.4U 0.5, the relative humidity of 100RH ~ (12) RH ~ (12) RH ~ (2 +) is used for 7 days. The effect of reducing shrinkage and its compatibility with superplasticizer were evaluated under the condition of 28d ~ 56d, and the effective action conditions of the reducer were determined. The effect of shrinkage reducer on the compressive strength of cement stone is also tested. The results show that the shrinkage reducing agent can significantly reduce the drying shrinkage of cement stone when it is added into the cement stone at the early age of 7 days. The shrinkage rate of SBT-SRA is 47.15 for cement stone with water-cement ratio of 0.3.The shrinkage reduction effect of shrinkage reducer brush and soaking method is not obvious. The maximum reduction rates were only 6.64% and 8.27 respectively. For the cement stone in the late curing period (56 d), the shrinkage reducing agent and the method of soaking the cement stone play a significant role in reducing the shrinkage. The maximum shrinkage rate is 45.53% and 30.88 respectively. The shrinkage reduction effect of the external brush is poor, and the shrinkage reduction rate is only 15.72. The compressive strength of cement stone can be reduced by adding shrinkage reducing agent. When the content of SBT-SRA is 0.2, the compressive strength of cement stone with 0.4 water-cement ratio is only 84.5% of the benchmark. The strength of cement stone is improved in different degree when the method of brush or immersion outside of reducing agent is used. Under the same condition, the compressive strength of cement stone for 28 days is slightly higher than that of the reference group. The main reason of reducing shrinkage is to reduce the surface tension of pore solution by adding a large amount of shrinkage reducer. At the same time, the shrinkage reduction agent can achieve the purpose of reducing shrinkage by reducing the evaporation rate (low humidity region) of pore solution. The shrinkage reducer is used to refine the pore structure of cement stone, so that the number of harmful pores is reduced and the drying shrinkage of cement stone is reduced. The total porosity of cement stone is increased when the shrinkage reducer is added. The total porosity of cement stone is reduced by brushing and soaking, and the three methods are used to refine the pore structure of cement stone. Under different humidity conditions, the shrinkage reduction mechanism of reducing agent is different: 85 RH in high humidity region. 75 RH and 55 RH, the shrinkage reducing agent is mainly to reduce the surface tension of the pore solution, thereby reducing the shrinkage stress caused by water evaporation to achieve the purpose of reducing shrinkage. In the low humidity region, the shrinkage reducing agent mainly reduces the total shrinkage stress caused by capillary water evaporation by reducing the evaporation rate of pore solution in cement stone. When GRA-SRA is co-mixed with polycarboxylic acid superplasticizer, it is in the humidity section of RHn85RH. Compared with the reference group, the cement stone expanded to a certain extent at 28 days, and the addition of GRA-SRA and polycarboxylic acid superplasticizer in the humidity section of 55RH and RH played a certain effect of reducing shrinkage. But it is not as good as the reduction effect of GRA-SRA alone. It can be seen that polycarboxylic acid superplasticizer has a certain negative effect on GRA-SRA shrinkage. Through the research on the mechanism of shrinkage reducer covering almost the whole humidity range and the evaluation of shrinkage effect under different action conditions, we can see that polycarboxylic acid superplasticizer has some negative effect on the shrinkage reduction of GRA-SRA. . This paper is of great theoretical significance for the research and development of shrinkage reducer and its application in practical engineering.
【學位授予單位】：重慶大學
【學位級別】：碩士
【學位授予年份】：2015
【分類號】：TU528.042

【相似文獻】

相關期刊論文 前10條

1 錢春香;耿飛;李麗;;減縮劑的作用及其機理[J];功能材料;2006年02期

2 周冬林;曹曉潤;;高性能混凝土減縮劑概述[J];河南建材;2006年03期

3 張志賓;徐玲玲;;水泥基材料復配減縮劑的減縮作用[J];硅酸鹽學報;2007年04期

4 王智;喬墩;錢覺時;石亮;;減縮劑外涂對水泥基材料性能的影響[J];硅酸鹽學報;2009年07期

5 錢覺時;喬墩;石亮;黨玉棟;王智;李有光;;減縮劑外涂對混凝土性能的影響及作用機理[J];硅酸鹽學報;2009年12期

6 任慧韜;郭磊;;減縮劑內(nèi)摻對水泥砂漿材料性能的影響[J];建筑科學與工程學報;2012年03期

7 任慧韜;郭磊;;減縮劑摻加對混凝土性能的影響[J];大連理工大學學報;2013年03期

8 林宗浩;王智;蔣長清;金衛(wèi)民;;減縮劑性能評價方法中的幾個問題探討[J];硅酸鹽通報;2013年08期

9 吳國輝;徐玲玲;張志賓;;減縮劑的合成與收縮性能[J];南京工業(yè)大學學報(自然科學版);2009年03期

10 高南簫;劉加平;冉千平;田倩;張建綱;;兩親性低分子聚醚減縮劑減縮機理探索[J];功能材料;2012年14期

相關會議論文 前10條

1 殷慶立;Lionel Raynaud;Pascal Taquet;;減縮劑對自流平材料收縮及其它性能的影響[A];第三屆全國商品砂漿學術交流會論文集[C];2009年

2 朱衛(wèi)東;趙青林;陳明輝;Stefan Stadtmüller;季偉;;減縮劑對混凝土性能影響實驗研究[A];第七屆全國混凝土耐久性學術交流會論文集[C];2008年

3 高南簫;冉千平;張建綱;繆昌文;劉加平;;新型接枝共聚物減縮劑的開發(fā)與研究[A];2011中國材料研討會論文摘要集[C];2011年

4 金恒剛;陳翠紅;王元;李景歡;;混凝土高性能減縮劑對混凝土裂縫控制的研究[A];高性能混凝土的研究與應用——第五屆全國高性能混凝土學術交流會論文[C];2004年

5 雷愛中;陳改新;王秀軍;宋保洪;曹建國;紀國晉;;減縮劑對混凝土性能的影響[A];中國硅酸鹽學會混凝土水泥制品分會第七屆理事會議暨學術交流大會論文集[C];2005年

6 陳美祝;何真;;減縮劑對水泥基材料早期性能的影響[A];中國硅酸鹽學會2003年學術年會論文摘要集[C];2003年

7 王元;陳翠紅;;減縮劑對混凝土塑性裂縫抑制作用的研究[A];混凝土外加劑及其應用技術[C];2004年

8 王元;陳翠紅;;減縮劑對混凝土塑性裂縫的抑制作用的研究[A];中國硅酸鹽學會混凝土水泥制品分會第七屆理事會議暨學術交流大會論文集[C];2005年

9 張志賓;徐玲玲;劉方;楊靜;章明;;減縮劑與水泥適應性的研究[A];第十屆全國水泥和混凝土化學及應用技術會議論文摘要集[C];2007年

10 吳浩;姚燕;王玲;;摻減縮劑水泥漿體水化產(chǎn)物生成的定量計算[A];中國建筑材料聯(lián)合會混凝土外加劑分會第十四次會員代表大會--“科隆杯”混凝土外加劑論文集（下冊）[C];2014年

相關重要報紙文章 前3條

1 王建國;新型混凝土減縮劑問世[N];中國建材報;2005年

2 郭關朝;混凝土抗裂減縮劑通過鑒定[N];中國建材報;2004年

3 俞國榮（作者單位：杭州萬藝建材有限公司）;混凝土收縮裂縫成因及預防措施[N];中國建材報;2004年

相關博士學位論文 前3條

1 喬春雨;礦物摻合料和減縮劑對混凝土傳輸性能的影響[D];北京科技大學;2016年

2 喬墩;減縮劑對水泥基材料收縮抑制作用及機理研究[D];重慶大學;2010年

3 黨玉棟;減縮劑與內(nèi)養(yǎng)護對水泥基材料體積穩(wěn)定性的影響[D];重慶大學;2012年

相關碩士學位論文 前10條

1 孟凡路;地溝油用于混凝土脫模劑與減縮劑的研究[D];哈爾濱工業(yè)大學;2015年

2 程正茂;混凝土減縮劑的作用機理與作用條件[D];重慶大學;2015年

3 代小妮;聚丙烯酸鹽類減縮劑的合成與性能研究[D];重慶大學;2008年

4 石亮;減縮劑外涂對水泥基材料性能影響的研究[D];重慶大學;2009年

5 蔣長清;聚丙烯酸鹽類減縮劑的合成及性能研究[D];重慶大學;2005年

6 方慶偉;減縮劑對水泥基材料性能的影響研究[D];浙江大學;2015年

7 王海驕;酯類聚羧酸減縮劑的研制與性能研究[D];北京建筑大學;2013年

8 羅白云;偶聯(lián)劑、減縮劑改性新老混凝土修補界面層的性能[D];汕頭大學;2003年

9 郭清春;聚羧酸減水劑與減縮劑的相容性研究[D];重慶大學;2012年

10 李磊;減縮防裂高性能混凝土外加劑的試驗研究[D];北京交通大學;2013年

，

本文編號：1490372