【摘要】：簡述了絕緣子用球墨鑄鐵附件的重要性,對其缺陷的危害程度進行了說明,通過對球墨鑄鐵附件的解剖,針對解剖出的孔洞缺陷從原料、工藝、工裝設備等方面進行了綜合分析,得出孔洞缺陷是球墨鑄鐵附件壁厚變化顯著和澆冒口設置不合理造成的,提出了改變澆冒口的形狀數(shù)量及大小、控制澆注時鐵液的溫度,提高砂型的剛度的改進措施,消除了球墨鑄鐵附件的孔洞缺陷。
[Abstract]:The importance of nodular cast iron accessories for insulators is briefly described, and the harm degree of defects is explained. through the anatomy of nodular cast iron accessories, the comprehensive analysis of the dissected hole defects is carried out from the aspects of raw materials, technology, tooling equipment and so on. It is concluded that the hole defects are caused by the remarkable change of wall thickness of nodular cast iron accessories and the unreasonable setting of risers, and the number and size of castable risers are changed. The hole defects of nodular cast iron accessories are eliminated by controlling the temperature of molten iron and improving the stiffness of sand mold.
【作者單位】： 中電普瑞科技有限公司;
【分類號】：TM216

【相似文獻】

相關期刊論文 前10條

1 林鵬;含裂紋與孔洞缺陷介質的脆性破壞行為[J];巖石力學與工程學報;2002年08期

2 唐艷麗;馬春學;盛文斌;張春明;張勇;蔣振峰;韓慶吉;;水射法制備鋼丸粒度及孔洞缺陷分布規(guī)律研究[J];山東理工大學學報(自然科學版);2010年01期

3 鄭麗娟;周紅梅;劉會瑩;付宇明;;含埋藏孔洞缺陷金屬構件電磁熱止裂強化分析[J];中國機械工程;2012年11期

4 徐志輝;杜希剛;張守豐;麻碩;;HT250鑄件表面孔洞缺陷分析[J];失效分析與預防;2011年04期

5 ;[J];;年期

6 ;[J];;年期

7 ;[J];;年期

8 ;[J];;年期

9 ;[J];;年期

10 ;[J];;年期

相關會議論文 前1條

1 陳偉;蘇鶴洲;李金柱;;昆鋼熱軋板孔洞缺陷成因淺析[A];第八屆全國連鑄學術會議論文集[C];2007年

相關重要報紙文章 前1條

1 記者 楊禮兵邋特約記者 白方;孔洞檢測儀察瑕疵于細微[N];湖北日報;2008年

相關碩士學位論文 前10條

1 徐華東;基于模態(tài)分析的紅松方材內部孔洞缺陷檢測[D];東北林業(yè)大學;2008年

2 于文勇;基于超聲波原木內部孔洞缺陷定量檢測[D];東北林業(yè)大學;2006年

3 張希棟;主要測試條件參數(shù)對原木孔洞缺陷應力波檢測效果的影響[D];東北林業(yè)大學;2007年

4 宋世全;基于支持向量機的原木樹種及原木內部孔洞缺陷辨識[D];東北林業(yè)大學;2012年

5 楊慧敏;基于能量法木材孔洞缺陷的超聲定量檢測研究[D];東北林業(yè)大學;2005年

6 黃濤;電鍍工藝優(yōu)化對銅金屬層孔洞缺陷的影響[D];上海交通大學;2010年

7 吳鵬;優(yōu)化銅種子層對電鍍銅孔洞缺陷的改善[D];復旦大學;2011年

8 符正晴;基于PNN的板材孔洞缺陷紅外熱波檢測及其識別技術[D];華東交通大學;2014年

9 孟憲靜;基于模糊模式識別的木材孔洞缺陷識別模型的研究[D];東北林業(yè)大學;2014年

10 李文軍;發(fā)動機曲軸鑄造孔洞缺陷的分析[D];吉林大學;2013年

，

本文編號：2503096