【摘要】：按JB/T7630.1對4種隔板樣品進行厚度、定量、孔率、最大孔徑、吸酸值和拉伸強度等測試,重點觀察隔板的微觀玻璃纖維結(jié)構(gòu),對比表面積、針刺強度、壓縮性和回彈性、彈性疲勞等進行分析。含短切纖維多的隔板,比表面積波動較大,拉伸強度和穿刺強度最小,壓縮性和回彈性最差,在高溫下易發(fā)生彈性疲勞;細纖維含量高的隔板綜合性能較佳。
[Abstract]:The thickness, quantity, porosity, maximum pore size, acid absorption value and tensile strength of four kinds of diaphragm samples were measured according to JB/T7630.1. The microstructure, specific surface area, needle punching strength, compressibility and elasticity of the diaphragm were observed. Elastic fatigue, etc. The diaphragm with short cut fiber has a large fluctuation of specific surface area, minimum tensile strength and puncture strength, and the worst compressibility and resilience, and is prone to elastic fatigue at high temperature, and the partition with high fiber content has better comprehensive properties.
【作者單位】： 浙江南都電源動力股份公司;
【分類號】：TM912.1

【參考文獻】

相關(guān)期刊論文 前5條

1 陳體銜,鄭君銑,張瑞恩;電池裝配壓力對玻璃纖維隔膜的影響[J];蓄電池;1996年02期

2 李福昭;鉛酸蓄電池隔板的現(xiàn)狀與發(fā)展[J];電池;1996年05期

3 華壽南,閻新華,馬建平;鉛酸蓄電池發(fā)展前瞻——第8屆歐洲鉛酸蓄電池會議的熱點問題評介(下)[J];電池;2004年01期

4 孫偉;超細玻璃棉隔板(AGM)比表面積計算公式推導(dǎo)[J];玻璃纖維;1998年06期

5 林長鋒;;淺析無堿與中堿玻璃纖維異同[J];21世紀建筑材料;2009年01期

【共引文獻】

相關(guān)期刊論文 前4條

1 朱雯娟;李卓球;;ECR和中堿玻璃纖維的耐酸性試驗[J];玻璃纖維;2010年04期

2 宿占寰;閥控式鉛酸蓄電池早期失效的原因分析[J];蓄電池;1997年04期

3 華壽南,朱教偉,王平;VRLA電池的AGM隔板和氧傳輸(1)[J];電池;2005年02期

4 包有富,張華,胡信國;AGM隔板性能對密封鉛酸蓄電池性能的影響[J];電源技術(shù);2000年05期

相關(guān)碩士學(xué)位論文 前3條

1 黃明香;汽車起動用鉛酸蓄電池極板化成及其性能的研究[D];福州大學(xué);2006年

2 李石;新型電動自行車用鉛酸蓄電池正極板柵合金的研究[D];華南師范大學(xué);2007年

3 楊曉娟;超高分子量聚乙烯電池膜成型研究[D];北京化工大學(xué);2012年

【二級參考文獻】

相關(guān)期刊論文 前4條

1 吳永坤,龔方紅,沙德仁;纖維玻璃耐堿性的研究[J];玻璃纖維;2004年04期

2 馬素卿;日本小型密封鉛酸蓄電池用隔板的改進[J];蓄電池;1991年01期

3 張維維;隔板結(jié)構(gòu)對閥控式電池性能的影響[J];蓄電池;1994年04期

4 華壽南,閻新華,馬建平;第8屆歐洲鉛蓄電池會議(8ELBC)回顧[J];蓄電池;2003年02期

，

本文編號：2377869