【摘要】：無(wú)磁性、高強(qiáng)度Ni-9.3at%W(Ni9W)合金由于其較低的層錯(cuò)能,難以通過(guò)傳統(tǒng)的軋制及再結(jié)晶退火得到強(qiáng)立方織構(gòu)。本工作采用熔煉制坯路線,結(jié)合均勻化退火和中間再結(jié)晶退火的方法得到了晶粒尺寸細(xì)小,合金元素W均勻分布的Ni9W坯錠,通過(guò)總變形量為99%的軋制,中間引入四次軋制間回復(fù)退火得到了厚度為80μm的Ni9W軋制基帶,最后采用兩步再結(jié)晶退火的方式得到了再結(jié)晶立方織構(gòu)含量為80.2%(10o)的Ni9W合金基帶。
[Abstract]:Because of its low stacking fault energy, it is difficult to obtain strong cubic texture by traditional rolling and recrystallization annealing in non-magnetic and high-strength Ni-9.3at%W (Ni9W) alloys. In this work, Ni9W billet with fine grain size and uniform distribution of alloying element W was obtained by melting process, combining homogenization annealing and intermediate recrystallization annealing, and the total deformation was 99%. The Ni9W rolling band with thickness of 80 渭 m was obtained by four times interrolling recovery annealing. Finally, the recrystallized cubic texture 80.2% (10o) Ni9W alloy substrate was obtained by two-step recrystallization annealing.
【作者單位】： 北京工業(yè)大學(xué)新型功能材料教育部重點(diǎn)實(shí)驗(yàn)室;
【基金】：國(guó)家自然科學(xué)基金(51171002) 北京市自然科學(xué)基金 北京市教育委員會(huì)科技計(jì)劃重點(diǎn)項(xiàng)目(KZ201310005003) 中央財(cái)政支持地方高校建設(shè)專項(xiàng)資金 北京市級(jí)創(chuàng)新團(tuán)隊(duì)建設(shè)提升計(jì)劃 211計(jì)劃專項(xiàng)資金
【分類號(hào)】：TM24

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 封國(guó)寧,陳紅波,李鐵球;方波懸汞催化伏安法連續(xù)測(cè)定U_3O_8中的Mo和W[J];鈾礦冶;1990年03期

2 王玟珉,Roth J,Lindig S,Wu CH;聚變反應(yīng)堆壁材料鎢和鉬的表面離子束效應(yīng)[J];核技術(shù);2003年06期

3 王巍;王曉磊;代作海;王穎;;不同金屬摻雜對(duì)TiO_2薄膜氧敏性能影響[J];電子質(zhì)量;2011年02期

4 肖代紅;宋e，

本文編號(hào)：2226755