本文選題：偏二氟乙烯-六氟丙烯共聚物 + 納米二氧化鈦��； 參考：《中南大學(xué)》2014年博士論文

【摘要】：摘要：與商品化的液態(tài)鋰離子電池相比,聚合物鋰離子電池具備較高的安全性、優(yōu)越的外形設(shè)計(jì)靈活性以及更高的質(zhì)量比能量,成為新一代鋰離子二次電池研究的熱點(diǎn)。開(kāi)發(fā)性能優(yōu)越的聚合物電解質(zhì)作為制備高性能聚合物鋰離子二次電池的有效途徑,已受到廣泛關(guān)注,其中,納米復(fù)合聚合物電解質(zhì)膜的研究成為開(kāi)發(fā)高性能聚合物電解質(zhì)重要方向之一。然而,由于納米無(wú)機(jī)顆粒極易團(tuán)聚,很難分散在聚合物電解質(zhì)基體,團(tuán)聚的納米粒子喪失了納米材料本身所具備的特性,其增強(qiáng)的聚合物電解質(zhì)膜性能受到限制。因此,本論文從根據(jù)分散的一般策略,從抑制納米顆粒團(tuán)聚的角度設(shè)計(jì)合成可用來(lái)增強(qiáng)PVDF-HFP凝膠型聚合物電解質(zhì)膜性能的納米Ti02有機(jī)-無(wú)機(jī)復(fù)合體,并對(duì)納米復(fù)合體合成制備工藝、聚合物復(fù)合電解質(zhì)膜的結(jié)構(gòu)與性能以及納米粒子增強(qiáng)聚合物電解質(zhì)膜電導(dǎo)機(jī)理展開(kāi)了研究,并取得以下研究成果： 1)為了克服納米Ti02顆粒之間的團(tuán)聚問(wèn)題,利用原位聚合與結(jié)晶的方法成功合成了高分散的納米TiO2-PMMA復(fù)合體,納米TiO2顆粒表面通過(guò)偶聯(lián)劑乙烯基三乙氧基硅烷“鍵橋作用”,接枝了PMMA分子層,抑制了納米Ti02團(tuán)聚。 2)以聚烯烴隔膜為支撐層,將原位合成的高分散納米TiO2-PMMA復(fù)合體與PVDF-HFP復(fù)合,制備出以聚烯烴隔膜為支撐層的夾層復(fù)合聚合物電解質(zhì)膜,并利用掃描電鏡、線性掃描伏安法、交流阻抗測(cè)試、充放電電池測(cè)試等表征手段對(duì)復(fù)合電解質(zhì)膜的結(jié)構(gòu)與性能進(jìn)行了研究。結(jié)果表明,在PVDF-HFP中添加高分散的納米TiO2-PMMA復(fù)合體,可顯著改善了PVDF-HFP聚合物電解質(zhì)膜的電池性能,特別是倍率性能。提高納米TiO：顆粒在PVDF-HFP聚合物復(fù)合電解質(zhì)膜中的分散性,可有效提高復(fù)合電解質(zhì)膜的離子電導(dǎo)率、電極相容性,從而起到增強(qiáng)聚合物復(fù)合電解質(zhì)膜的電池性能的效果,其中,電極相容性的改善是聚合物電池倍率性能得到提高的主要原因。 3)原位聚合與結(jié)晶的方法成功合成了單分散的納米TiO2@Li+單離子導(dǎo)體(TiO2-PAALi-PMMA),利用合成過(guò)程的酸堿反應(yīng),降低了納米Ti02分散能耗,有效提高了納米Ti02分散效率,得到單分散的單離子導(dǎo)體DMF分散液。 4)以PVDF-HFP靜電紡絲膜為支撐層,利用相分離法制備了單離子導(dǎo)體TiO2@Li+/PVDF-HFP復(fù)合電解質(zhì)膜,膜的厚度控制在45μm左右,復(fù)合電解質(zhì)膜具備較好的機(jī)械強(qiáng)度、抗熱收縮性能、電化學(xué)性能以及電池性能。其中,當(dāng)復(fù)合層納米單離子導(dǎo)體含量為50wt%時(shí),復(fù)合膜的斷裂強(qiáng)度達(dá)到39MPa,活化后的電解質(zhì)膜離子電導(dǎo)率達(dá)到3.63×10-S cm-1,離子遷移數(shù)為0.52,倍率性能和循環(huán)性能相對(duì)于PE隔膜電池均得到改善。 5)單分散的納米TiO2@Li+單離子導(dǎo)體分散在PVDF-HFP聚合物電解質(zhì)膜中存在“自組裝”行為。復(fù)合電解質(zhì)膜內(nèi)部的納米單離子導(dǎo)體向膜與電極接觸的界面以及基體內(nèi)膜孔內(nèi)表面離析與富集,富集在電解質(zhì)與電極界面的納米粒子增強(qiáng)了電極與電解質(zhì)的界面相容性,降低了界面電阻。富集在復(fù)合膜內(nèi)孔隙的納米粒子因雙電層效應(yīng)產(chǎn)生“快離子傳導(dǎo)通道”,從而起到提高聚合物復(fù)合電解質(zhì)膜離子電導(dǎo)率的效果。
[Abstract]:Abstract: compared with the commercialized liquid lithium ion battery, the polymer lithium ion battery has high safety, superior shape design flexibility and higher mass ratio of energy. It has become a hot spot in the research of the new generation of lithium ion two battery. The development of high performance polymer electrosolution is used as the preparation of high performance polymer lithium ion two times The effective ways of the battery have attracted much attention. Among them, the research of nanocomposite polymer electrolyte membrane has become one of the important directions for the development of high performance polymer electrolytes. However, it is difficult to disperse on the matrix of polymer electrolyte because of the easy aggregation of nano inorganic particles. The aggregation nanoparticles lose the special properties of nanomaterials themselves. The performance of the enhanced polymer electrolyte membrane is limited. Therefore, in this paper, the nano Ti02 organic-inorganic complex, which can be used to enhance the properties of the PVDF-HFP gel polymer electrolyte membrane, is designed and synthesized from the point of view of dispersing the agglomeration of nanoparticles. The structure and properties of electrolyte membrane and the conductivity mechanism of nanoparticle reinforced polymer electrolyte membrane have been studied.
1) in order to overcome the agglomeration of nano Ti02 particles, the highly dispersed nano TiO2-PMMA complex was successfully synthesized by in-situ polymerization and crystallization. The nano TiO2 particles were grafted by the coupling agent vinyl triethoxy silane "bond bridge", and the PMMA molecular layer was grafted to inhibit the nano Ti02 agglomeration.
2) the composite polymer electrolyte membrane with polyolefin membrane as the supporting layer was prepared by using polyolefin diaphragm as the supporting layer, and the polyolefin membrane as the supporting layer was prepared. The composite electrolyte membrane was characterized by scanning electron microscopy, linear scanning voltammetry, AC impedance testing, charge discharge battery test and other characterization means. The results show that the addition of highly dispersed nano TiO2-PMMA complexes in PVDF-HFP can significantly improve the battery performance of the PVDF-HFP polymer electrolyte membrane, especially the ratio performance. The enhancement of nano TiO: the dispersion of particles in the PVDF-HFP polymer electrolyte membrane can effectively improve the composite electrolyte. The ionic conductivity and electrode compatibility of the membrane can enhance the battery performance of the polymer composite electrolyte membrane, in which the improvement of the compatibility of the electrode is the main reason for the increase of the performance of the polymer battery.
3) the single dispersed nano TiO2@Li+ single ion conductor (TiO2-PAALi-PMMA) was successfully synthesized by in-situ polymerization and crystallization. Using the acid base reaction of the synthesis process, the energy consumption of nano Ti02 was reduced, and the dispersion efficiency of nano Ti02 was improved effectively, and monoionic monomer DMF dispersion was obtained.
4) the single ionic conductor TiO2@Li+/PVDF-HFP composite electrolyte membrane was prepared by phase separation method with the PVDF-HFP electrospun membrane as the supporting layer. The thickness of the membrane was controlled at about 45 m. The composite electrolyte membrane had good mechanical strength, thermal shrinkage resistance, electrochemical performance and electric pool performance. At 50wt%, the fracture strength of the composite membrane reaches 39MPa. The ionic conductivity of the electrolyte membrane after activation reaches 3.63 x 10-S cm-1 and the ion migration number is 0.52. The ratio and cycling performance of the membrane are improved compared with the PE membrane battery.
5) the single dispersed nano TiO2@Li+ single ion conductor is self assembled in the PVDF-HFP polymer electrolyte membrane. The interface of the nano single ion conductor to the membrane and the electrode in the composite electrolyte membrane, and the surface segregation and enrichment of the inner surface of the matrix, the nanoparticles enriched in the electrolyte and the electrode interface enhanced the electrode The interfacial compatibility with the electrolyte reduces the interfacial resistance. The nanoparticles enriched in the pores in the composite film produce the "fast ion conduction channel" due to the double layer effect, thus improving the ionic conductivity of the polymer composite electrolyte membrane.
【學(xué)位授予單位】：中南大學(xué)
【學(xué)位級(jí)別】：博士
【學(xué)位授予年份】：2014
【分類號(hào)】：TM912

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 杜洪彥,程琥,楊勇,林祖賡;可充鋰電池復(fù)合聚合物電解質(zhì)研究新進(jìn)展[J];電源技術(shù);2003年S1期

2 李朝暉,蘇光耀,高德淑,王霞瑜,李小平;硅鎢酸鋰在聚合物電解質(zhì)中的應(yīng)用[J];電源技術(shù);2004年12期

3 蔣晶;蘇光耀;;離子液體聚合物電解質(zhì)的研究進(jìn)展[J];電池;2005年06期

4 劉玉文,張勇,李小龍,顧琪萍,張翠芬,黃玉東;增塑聚合物電解質(zhì)電化學(xué)性能[J];電化學(xué);2005年01期

5 ;旭化成燃料電池高耐熱氟類聚合物電解質(zhì)[J];有機(jī)硅氟資訊;2005年10期

6 楊金鑫;孫方民;尹艷紅;岳紅云;楊偉光;楊書(shū)廷;;新型復(fù)合聚合物電解質(zhì)膜的制備及性能[J];電池;2006年02期

7 盧敏;張玉清;蘆雷鳴;;離子液體聚合物電解質(zhì)在染料敏化太陽(yáng)能電池中的應(yīng)用[J];化工之友;2007年17期

8 張記甫;桑商斌;伍秋美;;堿性聚合物電解質(zhì)的研究進(jìn)展[J];電池;2007年05期

9 谷芝元;魯?shù)罉s;許明;唐慧;;堿性固體聚合物電解質(zhì)膜的制備及性能研究[J];合肥工業(yè)大學(xué)學(xué)報(bào)(自然科學(xué)版);2010年06期

10 王風(fēng)彥;屈年瑞;王洪超;;堿性聚合物電解質(zhì)的應(yīng)用進(jìn)展及其改性研究[J];廣州化工;2012年07期

相關(guān)會(huì)議論文 前10條

1 譚海軍;王鋼;潘春躍;;無(wú)機(jī)粒子摻雜含硫聚合物電解質(zhì)的制備與性能[A];第七屆中國(guó)功能材料及其應(yīng)用學(xué)術(shù)會(huì)議論文集（第7分冊(cè)）[C];2010年

2 范麗珍;趙淑金;南策文;;PEO-LiClO_4-SiO_2復(fù)合型聚合物電解質(zhì)[A];中國(guó)硅酸鹽學(xué)會(huì)2003年學(xué)術(shù)年會(huì)論文摘要集[C];2003年

3 徐先華;潘春躍;馮慶;;PEO/LiClO_4/TiO_2復(fù)合聚合物電解質(zhì)的制備及電化學(xué)性能研究[A];第十二屆中國(guó)固態(tài)離子學(xué)學(xué)術(shù)會(huì)議論文集[C];2004年

4 陳作鋒;姜艷霞;孫世剛;;分子篩復(fù)合微孔型聚合物電解質(zhì)及其與負(fù)極相容性研究[A];第十三次全國(guó)電化學(xué)會(huì)議論文摘要集（上集）[C];2005年

5 李志明;魏建功;單峰;鄭震;王新靈;;多孔氟硅膠表面沉積納米SiO_2粒子新型聚合物電解質(zhì)[A];2007年全國(guó)高分子學(xué)術(shù)論文報(bào)告會(huì)論文摘要集（下冊(cè)）[C];2007年

6 徐先華;潘春躍;馮慶;;PEO/LiClO_4/TiO_2復(fù)合聚合物電解質(zhì)的導(dǎo)電性能研究[A];第十二屆中國(guó)固態(tài)離子學(xué)學(xué)術(shù)會(huì)議論文集稀土專輯[C];2004年

7 梁亮;王瑋;吳惠康;房晶瑞;鮑玉勝;;聚合物電解質(zhì)的研究與進(jìn)展[A];第六屆中國(guó)功能材料及其應(yīng)用學(xué)術(shù)會(huì)議論文集（4）[C];2007年

8 金蘭英;姜艷霞;廖宏剛;孫世剛;;離子液體增塑的聚合物電解質(zhì)紅外透射光譜研究[A];第十五屆全國(guó)分子光譜學(xué)術(shù)報(bào)告會(huì)論文集[C];2008年

9 戶獻(xiàn)雷;容敏智;阮文紅;章明秋;;本征型聚合物電解質(zhì)的制備與表征[A];中國(guó)化學(xué)會(huì)第28屆學(xué)術(shù)年會(huì)第18分會(huì)場(chǎng)摘要集[C];2012年

10 黃興蘭;楊克潤(rùn);譚斌;馬果;王公應(yīng);鄧正華;;一種特殊球狀結(jié)構(gòu)的聚合物電解質(zhì)薄膜的制備方法[A];第29屆全國(guó)化學(xué)與物理電源學(xué)術(shù)年會(huì)論文集[C];2011年

相關(guān)重要報(bào)紙文章 前2條

1 ;成都聚合物鋰離子電池隔膜項(xiàng)目通過(guò)鑒定[N];今日信息報(bào);2004年

2 本報(bào)實(shí)習(xí)記者　 郭宇;鋰電池在交通領(lǐng)域應(yīng)用初露鋒芒[N];中國(guó)工業(yè)報(bào);2006年

相關(guān)博士學(xué)位論文 前10條

1 凌志軍;鋰離子電池用磷酸酯型固體聚合物電解質(zhì)研究[D];清華大學(xué);2007年

2 王立仕;鋰離子電池納米復(fù)合聚合物電解質(zhì)的制備及性能研究[D];北京化工大學(xué);2009年

3 王占良;鋰離子電池用聚合物電解質(zhì)應(yīng)用基礎(chǔ)研究[D];天津大學(xué);2003年

4 李雪莉;聚合物電解質(zhì)隔膜及鋰負(fù)極性能研究[D];復(fù)旦大學(xué);2005年

5 高昆;微孔聚合物電解質(zhì)的制備及其增強(qiáng)改性的研究[D];哈爾濱工業(yè)大學(xué);2007年

6 杜洪彥;二次鋰電池納米復(fù)合聚合物電解質(zhì)的制備、表征及其離子導(dǎo)電機(jī)理研究[D];廈門大學(xué);2004年

7 張鵬;新型鋰離子電池聚合物電解質(zhì)制備及性能研究[D];復(fù)旦大學(xué);2010年

8 程琥;鋰二次電池聚合物電解質(zhì)的制備、表征及其相關(guān)界面性質(zhì)研究[D];廈門大學(xué);2007年

9 高楊文;聚氧化乙烯/堿金屬鹽聚合物電解質(zhì)結(jié)構(gòu)與分子動(dòng)力學(xué)的固體高分辨核磁共振研究[D];華東師范大學(xué);2011年

10 邱瑋麗;無(wú)機(jī)-有機(jī)聚合物電解質(zhì)的制備與應(yīng)用研究[D];復(fù)旦大學(xué);2005年

相關(guān)碩士學(xué)位論文 前10條

1 金蘭英;離子液體聚合物電解質(zhì)的制備及其性能研究[D];廈門大學(xué);2008年

2 朱昌寶;離子液體復(fù)合聚合物電解質(zhì)的制備和電化學(xué)性能研究[D];廈門大學(xué);2008年

3 黃雪原;凝膠型離子液體/聚合物電解質(zhì)的合成和性能研究[D];湖南師范大學(xué);2009年

4 高安安;含硫固態(tài)聚合物電解質(zhì)的合成、結(jié)構(gòu)表征及導(dǎo)電性能研究[D];中南大學(xué);2009年

5 高祥虎;聚偏氟乙烯基微孔聚合物電解質(zhì)的制備及電化學(xué)性能研究[D];西北師范大學(xué);2009年

6 劉毅;金屬空氣燃料電池聚合物電解質(zhì)的合成[D];哈爾濱理工大學(xué);2010年

7 樸金丹;聚合物電解質(zhì)的制備及應(yīng)用研究[D];武漢大學(xué);2005年

8 李月麗;堿性固體聚合物電解質(zhì)制備及電性能的研究[D];昆明理工大學(xué);2006年

9 蔣晶;凝膠型離子液體/聚合物電解質(zhì)的制備及其性能研究[D];湘潭大學(xué);2006年

10 王磊;單離子聚合物電解質(zhì)膜的制備及其結(jié)構(gòu)表征與性能研究[D];哈爾濱理工大學(xué);2006年

，

本文編號(hào)：2053866