本文選題：鋰離子電池　切入點(diǎn)：玻璃纖維無紡布　出處：《電池》2014年06期

【摘要】：以玻璃纖維無紡布為基體,用高分散聚甲基丙烯酸甲酯(PMMA)包覆納米Ti O2雜化材料(Ti O2@PMMA)進(jìn)行復(fù)合,制備玻璃纖維基復(fù)合聚合物電解質(zhì)膜。用SEM、熱收縮、交流阻抗和充放電測(cè)試等研究復(fù)合膜的結(jié)構(gòu)、熱尺寸穩(wěn)定性及電化學(xué)性能。玻璃纖維/Ti O2@PMMA納米復(fù)合膜可在120~380℃保持良好的尺寸穩(wěn)定性,活化后得到的復(fù)合聚合物電解質(zhì)膜在室溫下的離子電導(dǎo)率為2.88 m S/cm,與金屬Li電極保持良好的界面穩(wěn)定性。組裝的Li Co O2/Li扣式電池在2.75~4.20 V充放電,8.0 C放電比容量可達(dá)120 m Ah/g,以不同電流共循環(huán)200次,放電容量保持率為85%。
[Abstract]:Glass fiber composite polymer electrolyte membrane was prepared by coating nano-TiO _ 2 hybrid material (TIO _ 2) with high dispersion polymethyl methacrylate (PMMA) on glass fiber nonwoven fabric.The structure, thermal size stability and electrochemical properties of the composite films were investigated by means of SEM, thermal shrinkage, AC impedance and charge-discharge tests.The glass fiber / Ti O2@PMMA nanocomposite film can maintain good dimensional stability at 120,380 鈩，