本文選題：ZnO納米管　切入點(diǎn)：納米枝狀CdTe　出處：《化學(xué)學(xué)報(bào)》2014年01期 　論文類型：期刊論文

【摘要】：采用電化學(xué)方法首先在ITO導(dǎo)電玻璃上制備了一維有序ZnO納米管陣列,然后在ZnO納米管陣列上采用電化學(xué)方法沉積納米枝狀CdTe,形成了納米枝狀CdTe包覆ZnO納米管的CdTe@ZnO殼核式復(fù)合結(jié)構(gòu),最后在上述復(fù)合結(jié)構(gòu)中旋涂一層P3HT薄膜形成P3HT包覆的P3HT@CdTe@ZnO復(fù)合薄膜.以此復(fù)合薄膜為光活性層組裝成半導(dǎo)體敏化太陽電池,研究了該類電池的光電轉(zhuǎn)換性能,對(duì)該電池的工作原理進(jìn)行初步研究,所得太陽電池能量轉(zhuǎn)換效率最高達(dá)到1.38%.
[Abstract]:One-dimensional ordered ZnO nanotube arrays were prepared on ITO conductive glass by electrochemical method. Then the nanocrystalline CdTe was deposited on ZnO nanotube array by electrochemical method. The CdTe@ZnO shell core composite structure was formed by nano-dendritic CdTe coated ZnO nanotubes. Finally, P3HT thin films were spin-coated into P3HT films to form P3HT-coated CdTe ZnO composite films. The composite films were assembled as photoactive layers to form semiconductor sensitized solar cells. The working principle of the solar cell is studied. The energy conversion efficiency of the solar cell is as high as 1.38.
【作者單位】： 河北科技大學(xué)理學(xué)院;
【基金】：國家自然科學(xué)基金(Nos.21173065,20573031) 河北省自然科學(xué)基金(No.B2010000856) 河北科技大學(xué)博士啟動(dòng)基金(QD201050) 校立科研基金(XL201255)資助~~
【分類號(hào)】：TM914.4;O614.241

【參考文獻(xiàn)】

相關(guān)期刊論文 前4條

1 郝彥忠;王偉;;聚3-甲基噻吩修飾硫化物量子點(diǎn)連接納米結(jié)構(gòu)TiO_2膜的光電化學(xué)研究[J];化學(xué)學(xué)報(bào);2007年06期

2 郝彥忠;馬潔霞;孫寶;李英品;任聚杰;;TiO_2納米棒和CdSe納米棒復(fù)合膜與聚3-甲基噻吩雜化太陽能電池研究[J];化學(xué)學(xué)報(bào);2010年01期

3 郝彥忠;曹寅虎;孫寶;張彥輝;李英品;徐東升;李香玲;;P3HT/CdS/TiO_2/ZnO一維有序核殼式納米棒陣列的構(gòu)制及其在雜化太陽電池中的應(yīng)用研究[J];化學(xué)學(xué)報(bào);2012年10期

4 孫寶;郝彥忠;郭奮;李英品;羅沖;裴娟;申世剛;;P3HT修飾一維有序殼核式CdS/ZnO納米棒陣列復(fù)合膜的光電化學(xué)性能[J];物理化學(xué)學(xué)報(bào);2012年12期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 張慧;吳t，

本文編號(hào)：1585556