本文關(guān)鍵詞：沉淀劑對Mn-Zn鐵氧體納米粒子磁性能的影響　出處：《人工晶體學報》2014年01期 　論文類型：期刊論文

  更多相關(guān)文章： 錳鋅鐵氧體 納米材料 沉淀劑 磁性材料

【摘要】：本研究以氨水和碳酸氫銨混合物為沉淀劑,試圖在近中性環(huán)境下合成Mn-Zn鐵氧體納米粒子以進一步提高所制備材料的磁性能。結(jié)果表明:當沉淀劑由NaOH變?yōu)榘彼?碳酸氫銨混合物時,Mn-Zn鐵氧體納米粒子的沉降時間明顯縮短(15 min,約為NaOH沉淀劑的1/3)。所得材料的飽和磁化強度高達81.99 emu/g,比NaOH的提高近90%。同時,材料的矯頑力(Hc)也明顯降低至52.7 Oe,說明氨水+碳酸氫銨混合物是一種制備高性能Mn-Zn鐵氧體納米磁性材料的有效沉淀劑。
[Abstract]:In this study, the mixture of ammonia and ammonium bicarbonate was used as precipitant. Mn-Zn ferrite nanoparticles were synthesized in near neutral environment to further improve the magnetic properties of the prepared materials. The results show that when the precipitant is changed from NaOH to ammonium bicarbonate mixture of ammonia water. The deposition time of Mn-Zn ferrite nanoparticles was shortened by 15 minutes, which was about 1 / 3 of that of NaOH precipitator. The saturation magnetization of the obtained material was as high as 81.99 emu/g. At the same time, the coercivity of the material also decreased to 52.7 Oe. The results show that ammonium bicarbonate mixture is an effective precipitator for preparing high performance Mn-Zn ferrite nanomagnetic materials.
【作者單位】： 河北工業(yè)大學材料科學與工程學院;河北工業(yè)大學化工學院;
【基金】：河北省自然科學基金(E2011202192,12215122D) 天津市應用基礎(chǔ)及前沿技術(shù)研究計劃(12JCYBJC11600)
【分類號】：TM277
【正文快照】： 1引言錳鋅鐵氧體由于具有高的初始磁導率、飽和磁化強度、電阻率以及低的功率損耗而成為很重要的軟磁材料,其在變壓器、磁放大器、磁記錄以及功率轉(zhuǎn)換器等方面有著廣泛的應用[1-4]。研究發(fā)現(xiàn):納米錳鋅鐵氧體具有良好的磁熱性能和較低的居里溫度,是一種理想的自發(fā)控溫型腫瘤材

【參考文獻】

相關(guān)期刊論文 前7條

1 章林;王德平;姚愛華;黃文?;井奧洪二;;Zn~(2+)對MnZn鐵氧體結(jié)構(gòu)、磁性能和磁熱效應的影響[J];功能材料;2007年07期

2 王夢魁;溫敏錳鋅鐵氧體的材料組成與居里溫度的關(guān)系的研究[J];錦州師范學院學報(自然科學版);2001年04期

3 曾華s，

本文編號：1437778