本文選題：低溫固體氧化物燃料電池 + 復(fù)合電解質(zhì)�。� 參考：《稀有金屬材料與工程》2017年06期

【摘要】：通過聚丙烯酰胺溶膠-凝膠法合成了La_(0.9)Sr_(0.1)Ga_(0.8)Mg_(0.2)O_(2.85)(LSGM)粉體并與二元碳酸鹽復(fù)合,制備了新型LSGM-碳酸鹽復(fù)合電解質(zhì),從老化、循環(huán)和電池輸出三方面考察了LSGM-(Li/Na)_2CO_3復(fù)合電解質(zhì)的穩(wěn)定性。結(jié)果表明,在600℃/650 h的測(cè)試中,復(fù)合電解質(zhì)的電導(dǎo)率長(zhǎng)期穩(wěn)定在0.07~0.09 S·cm~(-1);在室溫~700℃循環(huán)中碳酸鹽基本沒有損失,電導(dǎo)率也較穩(wěn)定;以LSGM-20%(Li/Na)_2CO_3為復(fù)合電解質(zhì)的單電池在0.79 A·cm~(-2)恒流放電,960 min內(nèi)平均功率密度為285 m W·cm~(-2)。
[Abstract]:A new type of LSGM-(Li/Na)_2CO_3 composite electrolyte was synthesized by polyacrylamide sol-gel method. The LSGM-(Li/Na)_2CO_3 composite electrolyte was prepared from aging, cycling and battery output.The results show that the conductivity of the composite electrolyte is stable at 0.07 ~ 0.09 S cm ~ (-1) for a long time at 600 鈩，