【摘要】：采用超聲回波法對大曲率碳纖維增強樹脂基復合材料零件進行超聲A-掃描,并對缺陷進行定位。結(jié)合缺陷區(qū)域和非缺陷區(qū)域的細觀形貌金相圖、宏觀表面狀態(tài)以及厚度測量結(jié)果的對比分析,討論了缺陷形態(tài)與其回波波形特征的對應關系,以及缺陷可能的形成原因。結(jié)果表明,缺陷在細觀尺度上呈現(xiàn)多處分層、氣孔和孔隙密集缺陷,在宏觀尺度上表現(xiàn)為零件表面貧膠與厚度增厚。缺陷的性質(zhì)與超聲A-掃描的檢測結(jié)果相吻合,缺陷的位置集中在零件大曲率部位,其形成原因與復合材料制造工藝密切相關。
[Abstract]:Ultrasonic A-scan of large curvature carbon fiber reinforced resin matrix composite parts was carried out by ultrasonic echo method, and defects were located. Based on the microstructure metallograph, macro-surface state and thickness measurement results of defect region and non-defect region, the corresponding relationship between defect shape and echo waveform characteristics and the possible causes of defect formation are discussed. The results show that the defects are layered in many places on the meso-scale, and the pores and pores are dense. On the macro-scale, the defects are thin and thickened on the surface of the parts. The property of the defect is consistent with the results of ultrasonic A-scan. The position of the defect is concentrated in the part with large curvature, and the cause of its formation is closely related to the manufacturing process of the composite material.
【作者單位】： 沈陽飛機工業(yè)(集團)有限公司理化測試中心;沈陽飛機工業(yè)(集團)有限公司工程技術中心;
【分類號】：TB332;TQ327.3

【相似文獻】

相關期刊論文 前10條

1 龐明軍;陸怡;;《化機制造工藝》課程教學新法[J];高師理科學刊;2006年01期

2 ;日本開發(fā)新的樹脂制造工藝[J];中國建設信息;2001年24期

3 ;日本計劃開發(fā)新的樹脂制造工藝[J];橡塑技術與裝備;2002年04期

4 任召春;;脫乙烷塔冷凝器管束的制造工藝探討[J];煉油與化工;2012年05期

5 蘇友南;;殼聚糖制造工藝探討[J];中國石油和化工;2007年11期

6 馬曉;;預制型橡膠跑道及其制造工藝[J];橡膠工業(yè);2012年06期

7 楊凌垣;;SMC的制造工藝及成型技術[J];合成樹脂及塑料;1991年04期

8 張美云;王娟;;水果套袋紙制造工藝的研究[J];陜西科技大學學報;2007年03期

9 康士臣,牛海,林瑞廣;鈦制大直徑薄壁容器──脫酸塔制造工藝的研究[J];化工機械;1999年03期

10 Hélène Pora;;改進新一代疫苗制造工藝[J];生命科學儀器;2007年03期

相關碩士學位論文 前1條

1 范勝華;流能粉碎用于吸收藥制造工藝的研究[D];南京理工大學;2005年

，

本文編號：2465077