【摘要】：采用粉末冶金技術(shù)制備含不同質(zhì)量分數(shù)(0,5%,10%和15%)納米SiC顆粒增強的Ti-6Al-4V(Ti64)金屬基復(fù)合材料(MMCs),研究添加納米SiC顆粒對復(fù)合材料力學(xué)性能如硬度和抗壓強度的影響。結(jié)果表明,當(dāng)壓縮載荷為6.035 MPa時,復(fù)合材料具有最佳的相對密度(93.33%)。SEM顯微組織觀察結(jié)果表明,Ti64/5%SiC_p復(fù)合材料的潤濕性和結(jié)合力得到了提高。采用X射線衍射技術(shù)研究Ti64/SiC_p復(fù)合材料中納米SiC顆粒含量對其相組成的影響,并分析其力學(xué)性能與相組成的關(guān)系。含10%和15%SiC_p的復(fù)合材料由于脆性界面反應(yīng)產(chǎn)生了新相,此新相對復(fù)合材料的強度和硬度不利。Ti64/5%SiC_p金屬基復(fù)合材料的抗壓強度和硬度較高,因此5%SiC_p是此復(fù)合材料的最佳含量。
[Abstract]:Ti-6Al-4V (Ti64) metal-matrix composites containing 10% and 15% nanocrystalline SiC particles were prepared by powder metallurgy technique. The effect of adding nano-SiC particles on mechanical properties of composites such as hardness and compressive strength was studied. The results show that when the compression load is 6.035 MPa, the composite has the best relative density (93.33%). SEM microstructure). The results show that the wettability and adhesion of Ti64/5%SiC_p composite are improved. The effect of the content of nano-sized SiC particles on the phase composition of Ti64/SiC_p composites was studied by X-ray diffraction technique, and the relationship between the mechanical properties and the phase composition was analyzed. The composite containing 10% and 15%SiC_p produced a new phase due to the brittle interface reaction, which is unfavorable to the strength and hardness of the composite. The compressive strength and hardness of the Ti64/5%SiC_p metal matrix composite are higher, so 5%SiC_p is the best content of the composite.
【作者單位】： CISL Department
【基金】：CISL, Department of Physics, Annamalai University for the support in using AFM and SEM for experimentation
【分類號】：TB333

【參考文獻】

相關(guān)期刊論文 前2條

1 張煜梓;黃陸軍;劉寶璽;耿林;;新型網(wǎng)狀增強體分布的原位自生TiB_w/Ti6Al4V復(fù)合材料的熱變形行為(英文)[J];Transactions of Nonferrous Metals Society of China;2012年S2期

2 黃陸軍;崔喜平;耿林;付玉;;軋制變形對網(wǎng)狀結(jié)構(gòu)TiB_w/Ti復(fù)合材料組織與力學(xué)性能的影響(英文)[J];Transactions of Nonferrous Metals Society of China;2012年S1期

【共引文獻】

相關(guān)期刊論文 前4條

1 G.SIVAKUMAR;V.ANANTHI;S.RAMANATHAN;;納米SiC顆粒增強Ti-6Al-4V基復(fù)合材料的制備和力學(xué)性能（英文）[J];Transactions of Nonferrous Metals Society of China;2017年01期

2 葛英飛;徐九華;宦海祥;;溫度和應(yīng)變率對原位合成鈦基復(fù)合材料動態(tài)壓縮性能及破壞機制的影響[J];復(fù)合材料學(xué)報;2016年10期

3 Yuanfei Han;Hongqiang Duan;Weijie Lu;Liqiang Wang;Di Zhang;;Fabrication and characterization of laminated Ti-(TiB + La_2O_3)/Ti composite[J];Progress in Natural Science:Materials International;2015年05期

4 付彬國;王宏偉;鄒鶉鳴;魏尊杰;;鑄造Ti-1100-0.10B合金中原位合成TiB相的顯微組織表征（英文）[J];Transactions of Nonferrous Metals Society of China;2015年07期

【二級參考文獻】

相關(guān)期刊論文 前9條

1 張可敏;鄒建新;李軍;于治水;王慧萍;;TC4鈦合金表面激光熔覆法制備Y_2O_3顆粒增強Ni/TiC復(fù)合涂層(英文)[J];Transactions of Nonferrous Metals Society of China;2012年08期

2 孫宇;曾衛(wèi)東;趙永慶;韓遠飛;馬雄;;應(yīng)用智能方法建立Ti-6Al-2Zr-1Mo-1V合金的本構(gòu)關(guān)系(英文)[J];Transactions of Nonferrous Metals Society of China;2012年06期

3 許光輝;楊延清;馮廣海;黃斌;羅賢;陳彥;;熱處理對SiC/Ti-6Al-4V復(fù)合材料力學(xué)性能的影響[J];稀有金屬材料與工程;2011年08期

4 ;Microstructural characterization of titanium matrix composite coatings reinforced by in situ synthesized TiB + TiC fabricated on Ti6Al4V by laser cladding[J];Rare Metals;2010年05期

5 李建康;楊延清;原梅妮;羅賢;李麗麗;;Effect of properties of SiC fibers on longitudinal tensile behavior of SiC_f/Ti-6Al-4V composites[J];Transactions of Nonferrous Metals Society of China;2008年03期

6 ;Constitutive equation and hot deformation characteristic of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy with equiaxed microstructure[J];Rare Metals;2007年S1期

7 王蕊寧;奚正平;趙永慶;戚運蓮;;Hot deformation and processing maps of titanium matrix composite[J];Transactions of Nonferrous Metals Society of China;2007年S1期

8 王香;蓋鵬濤;;Effect of carbon content on microstructure and property of TiC/Ti-6Al-4V composites[J];Transactions of Nonferrous Metals Society of China;2007年S1期

9 曲銀化;孫建科;孟祥軍;;鈦合金等溫鍛造技術(shù)研究進展[J];鈦工業(yè)進展;2006年01期

【相似文獻】

相關(guān)期刊論文 前10條

1 蔣成禹,吳銘方,于治水,梁超;Ti基釬料真空釬焊Ti-6Al-4V[J];焊接技術(shù);2002年01期

2 黃淑陽;陶海林;王建斌;王田;;軋制工藝對Ti-6Al-4V鈦合金棒材組織和性能的影響[J];中國鈦業(yè);2012年04期

3 謝波;Ti-6Al-4V電子束焊接研究[J];稀有金屬合金加工;1977年06期

4 尤世武;熱軋Ti-6Al-4V的織構(gòu)分析[J];稀有金屬快報;2002年06期

5 楊玉玲;張多;劉常升;;低功率激光焊接方法在Ti-6Al-4V焊接中的應(yīng)用[J];應(yīng)用激光;2006年06期

6 籍龍波;胡樹兵;李行志;王亞軍;陳冀彥;肖建中;;微量氫對電子束焊接Ti-6Al-4V鈦合金疲勞壽命的影響[J];材料熱處理學(xué)報;2011年06期

7 邵軍;朱玉香;;Ti-6Al-4V鈦合金棒材α層厚度的測定[J];中國鈦業(yè);2011年01期

8 謝志平;權(quán)變利;;基于信噪比的電火花加工Ti-6Al-4V加工工藝參數(shù)優(yōu)化[J];煤礦機械;2011年08期

9 吳會強,馮吉才,何景山,張秉剛;電子束焊接Ti-6Al-4V接頭斷裂行為機制[J];焊接學(xué)報;2004年04期

10 張平則,徐重,張高會,張艷梅,吳紅艷,姚正軍;純Ti及Ti-6Al-4V雙層輝光離子滲Mo[J];南京航空航天大學(xué)學(xué)報;2005年05期

相關(guān)會議論文 前4條

1 鎖紅波;陳哲源;李晉煒;;電子束熔融快速制造Ti-6Al-4V的力學(xué)性能[A];第13屆全國特種加工學(xué)術(shù)會議論文集[C];2009年

2 王力;張國偉;郭雨龍;邵東向;郭永豐;;鈦合金Ti-6Al-4V的電火花加工試驗研究[A];第15屆全國特種加工學(xué)術(shù)會議論文集（上）[C];2013年

3 杧美源;蔡履文;;Ti-6Al-4V雷射挷件高n笨赺7度奤估[A];2010年海峽兩岸材料破壞/斷裂學(xué)術(shù)會議暨第十屆破壞科學(xué)研討會/第八屆全國MTS材料試驗學(xué)術(shù)會議論文集[C];2010年

4 趙忠民;張龍;宋義剛;黃雪剛;張翼飛;張昊;;TiB_2基多相陶瓷與Ti-6Al-4V熔化連接及其層狀復(fù)合材料制備研究[A];第十七屆全國高技術(shù)陶瓷學(xué)術(shù)年會摘要集[C];2012年

相關(guān)碩士學(xué)位論文 前6條

1 楊奔峰;Ti-6Al-4V表面Ti（C、N）復(fù)合膜的液相等離子體制備工藝研究[D];南京理工大學(xué);2015年

2 黃達;Ti-6Al-4V與ZQSn10-10異種材料的擴散連接[D];吉林大學(xué);2006年

3 趙新鵬;高速切削Ti-6Al-4V切削力仿真研究[D];天津大學(xué);2010年

4 馮吉路;鈦合金Ti-6Al-4V高速切削絕熱剪切特征的研究[D];沈陽理工大學(xué);2013年

5 程信林;Ti-6Al-4V絕熱剪切形變中熱/力學(xué)參量的數(shù)值模擬及其剪切帶內(nèi)微觀組織演化機制的探討[D];中南大學(xué);2004年

6 唐明;熱處理組織對Ti-6Al-4V鈦合金銑削加工性能的影響[D];沈陽航空航天大學(xué);2013年

，

本文編號：2276768