本文選題：CIVA仿真軟件 + X射線成像檢測(cè)　； 參考：《玻璃鋼/復(fù)合材料》2017年02期

【摘要】：采用CIVA仿真模擬軟件,模擬不同檢測(cè)電壓、檢測(cè)電流和焦點(diǎn)尺寸下碳纖維樹(shù)脂基復(fù)合材料制品內(nèi)部分層缺陷的X射線成像檢測(cè)結(jié)果,得到最佳射線源工藝參數(shù);將最佳射線源工藝參數(shù)應(yīng)用于X射線錐束CT成像仿真模擬,與含分層缺陷的碳纖維樹(shù)脂基復(fù)合材料制品的X射線錐束CT成像檢測(cè)結(jié)果相比,仿真結(jié)果與實(shí)際檢測(cè)結(jié)果相吻合;同時(shí),通過(guò)實(shí)際碳纖維樹(shù)脂基復(fù)合材料制品的X射線錐束CT成像檢測(cè)結(jié)果驗(yàn)證了該最佳射線源工藝參數(shù)的可行性和可靠性。
[Abstract]:CIVA simulation software was used to simulate the X-ray imaging results of delamination defects in carbon fiber resin matrix composite products under different detection voltages, current and focus sizes, and the optimum technological parameters of the radiation sources were obtained. The optimum technological parameters of X-ray source are applied to the simulation of X-ray cone-beam CT imaging. Compared with the X-ray cone-beam CT imaging results of carbon fiber resin matrix composite products with delamination defects, the simulation results are in good agreement with the actual results. At the same time, the feasibility and reliability of the optimum radiation source parameters are verified by the X-ray cone-beam CT imaging of the carbon fiber resin matrix composite products.
【作者單位】： 中國(guó)兵器工業(yè)集團(tuán)第五三研究所;
【分類(lèi)號(hào)】：TB332

【相似文獻(xiàn)】

相關(guān)期刊論文 前7條

1 陳樹(shù)越,路宏年;數(shù)字式X射線成像無(wú)損檢測(cè)技術(shù)[J];華北工學(xué)院學(xué)報(bào);1999年01期

2 徐遙;;計(jì)算機(jī)X射線成像系統(tǒng)用于鋼管焊縫檢測(cè)技術(shù)通過(guò)鑒定[J];鋼管;2009年06期

3 汪希偉;洪冠;潘一凡;居榮華;趙茂程;;X射線成像系統(tǒng)及其在屏蔽包裝食品檢測(cè)中的應(yīng)用[J];包裝與食品機(jī)械;2007年04期

4 張文軍;;基于X射線成像的輸送帶內(nèi)部鋼絲故障診斷系統(tǒng)[J];煤炭科學(xué)技術(shù);2010年09期

5 劉賓;王黎明;蘇新彥;;高動(dòng)態(tài)范圍X射線成像檢測(cè)方法[J];光譜學(xué)與光譜分析;2014年04期

6 李發(fā)國(guó);東青;張佼;戴永兵;付亞楠;謝紅蘭;尹付成;孫寶德;;同步輻射X射線成像法原位研究Al-15%Cu合金柱狀晶-等軸晶轉(zhuǎn)變以及無(wú)軸柱狀枝晶生長(zhǎng)(英文)[J];Transactions of Nonferrous Metals Society of China;2014年07期

7 ;[J];;年期

相關(guān)會(huì)議論文 前3條

1 王煥玉;張承模;陳勇;梁小華;曹學(xué)蕾;汪錦州;高e，

本文編號(hào)：1924114