本文選題：竹纖維　切入點：竹塑復(fù)合　出處：《塑料》2017年01期

【摘要】：采用微生物法對竹纖維進行改性,研究其對竹纖維成分及結(jié)構(gòu)的影響,通過熱壓成型制備了不同竹塑配比的竹纖維增強聚丙烯復(fù)合材料(PP/BF),并對其力學(xué)性能、斷面微觀結(jié)構(gòu)進行表征來探討竹纖維對聚丙烯基體的增強性能。結(jié)果表明:微生物改性能有效去除纖維素表面部分的半纖維素、木質(zhì)素等成分,并在一定程度上降低了竹纖維的極性,改善了竹纖維與聚丙烯基體的界面浸潤性。所得的竹塑復(fù)合材料以竹纖維添加量為30%時,力學(xué)性能最優(yōu),其拉伸強度、彈性模量較純聚丙烯材料分別增強了3.4%、29.4%,彎曲強度、彎曲模量分別提高了38.9%、37.5%。
[Abstract]:The bamboo fiber was modified by microorganism method, and its effect on the composition and structure of bamboo fiber was studied. The PP / BF / PP composites with different bamboo / plastic ratio were prepared by hot pressing, and the mechanical properties of the composites were also studied. The microstructures of bamboo fibers on polypropylene matrix were characterized. The results showed that microbial modification could effectively remove hemicellulose and lignin from cellulose surface. To some extent, the polarity of bamboo fiber was reduced, and the interfacial wettability of bamboo fiber and polypropylene matrix was improved. Compared with pure polypropylene, the elastic modulus was increased by 3.4% and 29.4 respectively, and the flexural strength and flexural modulus were increased by 38.9% and 37.5% respectively.
【作者單位】： 浙江工業(yè)大學(xué)分析測試中心;國家林業(yè)局竹子研究開發(fā)中心;浙江省竹子高效加工重點實驗室;
【基金】：浙江省省院合作林業(yè)科技項目(2013SY05)
【分類號】：TB332

【參考文獻】

相關(guān)期刊論文 前3條

1 金秋;陳立華;閆少鋒;;有效微生物技術(shù)在城市環(huán)境治理領(lǐng)域中的應(yīng)用[J];環(huán)境科技;2015年01期

2 李達;姜媛媛;牛春華;;木質(zhì)纖維素類原料預(yù)處理工藝的研究[J];農(nóng)產(chǎn)品加工(學(xué)刊);2008年04期

3 鄧海波;林鹿;黃偉韓;;木質(zhì)纖維氨化反應(yīng)及其結(jié)構(gòu)變化[J];中國造紙學(xué)報;2007年04期

【共引文獻】

相關(guān)期刊論文 前10條

1 熊小藝;于輝;鄭遺凡;葉曉丹;鐘哲科;;竹纖維微生物改性對竹塑復(fù)合材料性能的影響[J];塑料;2017年01期

2 薛明霞;;微生物技術(shù)在山西冶金污染治理中的應(yīng)用研究[J];山西冶金;2016年06期

3 于陽陽;于少亭;張淑君;馮騫;王蕭;閆玉濤;鐘天意;;不同曝氣強度下SBR污染物去除性能研究[J];環(huán)境科技;2017年01期

4 張安龍;周丹妮;杜飛;郗文君;;生物促生劑對廢紙造紙活性污泥胞外聚合物的影響[J];中國造紙;2017年01期

5 姜波;;微生物技術(shù)在市政環(huán)境方面的應(yīng)用分析[J];科技創(chuàng)新與應(yīng)用;2016年17期

6 閆嘯;孫秀s，

本文編號：1692885