本文關(guān)鍵詞： 電工鋼條帶 輥速 鉻元素 熔體旋淬法　出處：《熱加工工藝》2017年10期 　論文類型：期刊論文

【摘要】：利用熔體旋淬法采用不同輥速制得含Cr電工鋼條帶,并通過金相顯微鏡、XRD、顯微硬度對加Cr前后的條帶組織和性能進行研究。結(jié)果表明:隨著輥速的增加,Fe-6.5%Si電工鋼條帶的組織均勻性增大,韌性增強;Cr元素可細化Fe-6.5%Si電工鋼條帶的晶粒尺寸,同時提高其強度和塑韌性;利用熔體旋淬法制備添加適量Cr的Fe-6.5%Si條帶,并配以較高的輥速是一種可行的方法。
[Abstract]:The speed was Cr containing electrical steel strip with different roll by melt spinning method, and through optical microscope, XRD, microhardness of Cr before and after the strip microstructure and properties were studied. The results showed that with the increase of roller speed, Fe-6.5%Si electrical steel strip microstructure uniformity increases and the toughness enhancement; Cr element refinement of Fe-6.5%Si electrical steel strip with the grain size, and improve its strength and toughness; Fe-6.5%Si bands by adding appropriate amount of Cr by using melt spinning, and with high speed and is a feasible method.

【作者單位】： 濰坊科技學院汽車工程學院;
【分類號】：TM275
【正文快照】： 電工鋼被廣泛應用于電力行業(yè),為我國電力事業(yè)的發(fā)展做出了極大貢獻。電工鋼的優(yōu)異磁性能來源于其成分中的Si含量,目前常用的電工鋼Si含量在4%以內(nèi),有研究表明[1-3]:當Si含量提升至6.5%,電工鋼能獲得最優(yōu)的磁性能,但由于硅含量的增高,材料的脆性急劇增大[4],常溫下根本無法采用，

本文編號：1455431