本文關鍵詞： 鋼-竹組合構(gòu)件 鋼-竹界面 長期荷載 推出試驗 黏結(jié)性能　出處：《建筑結(jié)構(gòu)學報》2017年09期 　論文類型：期刊論文

【摘要】：為研究鋼-竹組合構(gòu)件長期荷載作用后的整體工作性能,針對純膠結(jié)型界面與復合膠結(jié)型界面共27個鋼-竹界面試件進行了長期荷載作用后的推出試驗,以界面形式、長期持荷水平以及持荷時間為基本參數(shù),對鋼-竹界面的承載力、黏結(jié)應力及相對滑移進行了分析。研究表明:鋼-竹界面構(gòu)造形式合理,具有較高的承載能力,長期荷載作用后試件界面完整性良好,復合膠結(jié)型界面試件的破壞具有顯著的延性特征;2組純膠結(jié)型界面試件在長期荷載作用后承載力發(fā)生衰減,衰減系數(shù)分別為0.91與0.81;純膠結(jié)型界面的剪應力與相對滑移分布具有"兩端大、中間小"的特征,2組試件界面最大剪應力分別為1.41 MPa和1.25 MPa,與短期荷載作用后試件相比,約衰減10%和20%,界面的相對滑移則略有增長;長期荷載作用后復合膠結(jié)型界面的承載力、黏結(jié)應力及相對滑移與短期荷載作用后試件相比,未發(fā)生顯著變化,自攻螺釘可有效提高界面抗剪能力,按間距80 mm加設自攻螺釘后,界面最大剪應力可達到1.7 MPa。提出了長期荷載作用后的鋼-竹界面黏結(jié)承載力計算方法,其計算結(jié)果與試驗結(jié)果吻合較好。
[Abstract]:In order to study the overall performance of steel-bamboo composite members after long term load, 27 specimens with pure cemented interface and composite cemented interface were tested after long term load. The bearing capacity, bond stress and relative slip of the steel-bamboo interface are analyzed with the interface form, long-term load holding level and holding time as the basic parameters. The results show that the structural form of the steel-bamboo interface is reasonable. It has high bearing capacity, good interfacial integrity after long-term loading, and the failure of composite cemented interface specimens has obvious ductility characteristics. The bearing capacity of two groups of pure cemented interface specimens attenuates after long term load with attenuation coefficients of 0.91 and 0.81respectively. The shear stress and relative slip distribution of pure cemented interface are 1. 41 MPa and 1. 25 MPa, respectively. Compared with the specimen subjected to short term load, the attenuation is about 10% and 20, and the relative slip of the interface increases slightly. The bearing capacity, bond stress and relative slip of the composite cemented interface after long term load have not changed significantly compared with those of the specimen after short term load. The self-tapping screw can effectively improve the shear resistance of the interface. The maximum shear stress of the interface can reach 1.7 MPA after the self-tapping screw is added at the distance of 80mm. A method for calculating the adhesion capacity of the steel-bamboo interface under long-term loading is proposed. The calculated results are in good agreement with the experimental results.
【作者單位】： 寧波大學建筑工程與環(huán)境學院;肯特州立大學建筑與環(huán)境設計學院;
【基金】：國家自然科學基金項目(51378265,51678310) 寧波市自然科學基金項目(2017A610305)
【分類號】：TU398.9
【正文快照】： 2.肯特州立大學建筑與環(huán)境設計學院,俄亥俄肯特44242)0引言鋼-竹組合構(gòu)件是以改性竹材與薄壁型鋼為主要材料,通過結(jié)構(gòu)膠與自攻螺釘將兩者復合而成,可充分發(fā)揮兩種材料的優(yōu)勢,有利于生態(tài)平衡及能源節(jié)約。近年來,隨著環(huán)境問題的日益突出,竹材、木材等環(huán)境友好型建筑材料的應用受

【相似文獻】

相關期刊論文 前6條

1 吳東岳;張敏;凌志彬;;考慮界面相對滑移的鋼-混凝土組合梁力學性能分析[J];華東交通大學學報;2010年06期

2 周勇超;李亮亮;李子青;;鋼-混凝土組合梁界面滑移效應變分法求解[J];長安大學學報(自然科學版);2013年01期

3 張建文;曹雙寅;;型鋼輕骨料混凝土界面相對滑移研究[J];建筑科學;2010年05期

4 郭紅梅,徐利明;帽型截面鋼—混凝土組合梁變形計算公式[J];中外建筑;2003年05期

5 周勇超;李常樂;孫鐵軍;李子青;;鋼-混凝土組合梁界面滑移與剪力滯耦合效應分析[J];建筑科學與工程學報;2013年02期

6 鄭巨清;預制構(gòu)件中預應力筋與混凝土相對滑移的簡易測定[J];建筑施工;1994年03期

相關碩士學位論文 前1條

1 胡紅兵;C型外包花紋鋼—混凝土組合梁滑移性能試驗研究[D];合肥工業(yè)大學;2014年

，

本文編號：1471321