本文關(guān)鍵詞：高摻量粉煤灰PVA-ECC的力學(xué)性能研究及粉煤灰作用機理分析　出處：《硅酸鹽通報》2017年11期 　論文類型：期刊論文

  更多相關(guān)文章： 粉煤灰 ECC 纖維長度 力學(xué)性能

【摘要】：主要研究了高摻量粉煤灰對PVA-ECC力學(xué)性能的影響,對粉煤灰摻量分別為40%、50%、60%情況下PVAECC的抗壓強度、薄板四點彎曲性能等進行試驗研究,并分析了粉煤灰在ECC中的作用機理。結(jié)果表明:隨著粉煤灰摻量的增加,ECC的抗壓強度呈降低趨勢,四點彎曲試驗中ECC試件的初裂荷載和峰值荷載降低,跨中撓度增加,且裂縫寬度減小;高摻量粉煤灰下,纖維長度對ECC抗壓強度和延性有較大的影響,摻12 mm纖維的PVA-ECC在保證強度的同時,可獲得較高的延性和韌性。
[Abstract]:The effect of high fly ash content on the mechanical properties of PVA-ECC was studied. The compressive strength of PVAECC was 60% under the content of 40% fly ash. The four-point bending properties of thin plates were studied and the mechanism of fly ash in ECC was analyzed. The results showed that the compressive strength of ECC decreased with the increase of fly ash content. In the four-point bending test, the initial crack load and peak load of the ECC specimen are reduced, the mid-span deflection is increased, and the crack width is decreased. The fiber length has a great influence on the compressive strength and ductility of ECC under the condition of high fly ash content. The ductility and ductility of PVA-ECC doped with 12mm fiber can be obtained at the same time as the strength is guaranteed.
【作者單位】： 江南大學(xué)環(huán)境與土木工程學(xué)院;
【基金】：國家自然科學(xué)基金面上項目(51274105)
【分類號】：TU528
【正文快照】： 1引言混凝土具有原材料易獲取、加工制作簡單和抗壓強度高等優(yōu)點,成為建筑工程中使用最為廣泛的工程材料之一。但是混凝土具有抗拉強度低、脆性大和抗裂性能差等缺點,這些缺點易引起混凝土的開裂,混凝土開裂后易造成混凝土保護層的剝落和鋼筋銹蝕,從而影響結(jié)構(gòu)耐久性,降低結(jié)構(gòu)

【相似文獻】

相關(guān)期刊論文 前10條

1 包亦望;孫立;邱巖;;陶瓷力學(xué)性能綜合評價技術(shù)與分析軟件[J];稀有金屬材料與工程;2009年S2期

2 Helga Szibor;Hans W.Hennicke;王振林;徐如恬;;瓷材料的顯微結(jié)構(gòu)數(shù)據(jù)與力學(xué)性能之間的關(guān)系(第Ⅱ部分)[J];中國電瓷;1984年04期

3 包亦望;;陶瓷及玻璃力學(xué)性能評價的一些非常規(guī)技術(shù)[J];硅酸鹽學(xué)報;2007年S1期

4 楊巍屹;馬南鋼;;3YPSZ-Al_2O_3-Co_3O_4陶瓷力學(xué)性能的研究[J];中國陶瓷;2012年12期

5 魏超平;對嵌裝式裝飾石膏板力學(xué)性能的研究[J];新型建筑材料;1996年03期

6 付強,周萘,黃文e，

本文編號：1437157