【摘要】：采用高濃度硝酸銀溶液為銀源,以抗壞血酸為還原劑,聚乙烯吡咯烷酮為分散劑,制備超細銀粉,用掃描電子顯微鏡和振實密度測試儀對銀粉進行表征。結(jié)果表明,提高硝酸銀溶液濃度的同時,調(diào)整抗壞血酸和分散劑PVP的加入量,能夠獲得類球形、粒徑分布窄的銀粉顆粒,分散劑的種類和用量仍需進一步優(yōu)化。
[Abstract]:Ultrafine silver powder was prepared by using high concentration silver nitrate solution as silver source, ascorbic acid as reducing agent and polyvinylpyrrolidone as dispersant. The silver powder was characterized by scanning electron microscope and vibratory density tester. The results showed that when the concentration of silver nitrate solution was increased and the amount of ascorbic acid and dispersant PVP was adjusted, the spherical silver particles with narrow particle size distribution could be obtained. The type and amount of dispersant needed to be further optimized.
【作者單位】： 西北有色金屬研究院;
【分類號】：TF123.2

【相似文獻】

相關(guān)期刊論文 前10條

1 江建軍,談定生,劉久苗,韓月香,陳華,余仲興;葡萄糖還原制取超細銀粉[J];上海有色金屬;2004年01期

2 方立;;高分散超細銀粉[J];上海金屬.有色分冊;1987年05期

3 酈希;超細銀粉的制備及應(yīng)用[J];湖南化工;1994年04期

4 韋群燕,謝剛,李榮興,楊項軍,譚富彬;化學(xué)沉淀制備超細銀粉及其形貌特征[J];云南冶金;2004年01期

5 田曉霞;傅振堂;張超;王玉璽;申建;;利用廢定影液制備超細銀粉[J];信息記錄材料;2009年03期

6 甘衛(wèi)平;陳志波;陳迎龍;郭桂全;羅賤;;以聚丙烯酸為分散劑制備高分散超細銀粉[J];電子元件與材料;2011年10期

7 郭桂全;甘衛(wèi)平;羅賤;向鋒;張金玲;周華;劉歡;;正交設(shè)計法優(yōu)化高分散超細銀粉的制備工藝[J];稀有金屬材料與工程;2011年10期

8 宋永輝,蘭新哲,張秋利;超聲波強化制備超細銀粉[J];稀有金屬;2005年04期

9 郭學(xué)益;焦翠燕;鄧多;田慶華;易宇;;硝酸銀溶液性質(zhì)對超細銀粉形貌與粒徑的影響[J];粉末冶金材料科學(xué)與工程;2013年06期

10 蘭堯中;劉進;李現(xiàn)強;周建國;;水合肼還原法制備超細銀粉的研究[J];貴金屬;2005年04期

相關(guān)會議論文 前1條

1 路承杰;李玉杰;楊克勇;萬耿杰;馬騫;閆忠強;;超細銀粉的制備現(xiàn)狀概述[A];低碳經(jīng)濟條件下重有色金屬冶金技術(shù)發(fā)展研討會——暨重冶學(xué)委會第六屆委員會成立大會論文集[C];2010年

相關(guān)碩士學(xué)位論文 前1條

1 焦翠燕;液相還原法制備高品質(zhì)超細銀粉研究[D];中南大學(xué);2013年

，

本文編號：2283117