本文選題：鈷鉻鉬鎢合金粉末 + 氣霧化　； 參考：《粉末冶金材料科學(xué)與工程》2017年01期

【摘要】：利用自行研制的防返風(fēng)超音速氣霧化設(shè)備制備鈷鉻鉬鎢合金粉末,對粉末的形貌、粒度與粒度分布以及顯微組織等進行分析,并研究其激光選區(qū)熔化成形件的顯微組織、硬度和拉伸性能。結(jié)果表明,氣霧化制備的Co Cr Mo W合金粉末主要為球形,部分有衛(wèi)星顆粒,粉末組織由胞狀晶和樹枝晶組成。激光選區(qū)熔化成形的成形件表面熔道搭接良好,表面粗糙度為11.0μm,相對密度達到98.7%,組織為γ馬氏體和ε馬氏體;抗拉強度為1 283 MPa,屈服強度為852 MPa,伸長率為7.9%,顯微硬度HV達到398.8;拉伸斷口呈現(xiàn)準(zhǔn)解理斷裂特征。
[Abstract]:Cobalt chromium-molybdenum tungsten alloy powder was prepared by using the self-made anti-wind supersonic atomization equipment. The morphology, particle size and distribution and microstructure of the powder were analyzed, and the microstructure of the laser selective melting forming part was studied. Hardness and tensile properties. The results show that the Co Cr Mo W alloy powder prepared by gas atomization is mainly spherical, some of which are satellite particles, and the structure of the powder is composed of cellular crystal and dendrite. The surface melt channel of the formed parts formed by laser selective melting is good, the surface roughness is 11.0 渭 m, the relative density is 98.7, and the microstructure is 緯 martensite and 蔚 martensite. The tensile strength is 1 283 MPA, the yield strength is 852 MPA, the elongation is 7.9, the microhardness HV is 398.8, and the tensile fracture is quasi-cleavage fracture.
【作者單位】： 華南理工大學(xué)國家金屬近凈成形工程技術(shù)研究中心;江西悅安超細金屬有限公司;廣州市越瓏金屬粉末有限公司;
【基金】：廣東省科技攻關(guān)項目(2014B010129003) 廣東省自然科學(xué)基金團隊項目(2015A030312003) 廣州市科技攻關(guān)項目(201605101612300)
【分類號】：TF123.71

【相似文獻】

相關(guān)期刊論文 前8條

1 朱琦;王林;楊秦莉;王娜;;鉬鎢合金的組織和性能研究[J];中國鉬業(yè);2013年05期

2 于波;;鉬鎢合金腐蝕層的輝光光譜逐層分析[J];光譜學(xué)與光譜分析;1983年01期

3 李玲玲;電阻率和加工性能好的鉬鎢合金材料[J];中國鎢業(yè);1997年03期

4 楊揚;鉬及碳含量對鈮鉬鎢合金高溫機械性能的影響[J];稀有金屬與硬質(zhì)合金;2005年03期

5 鐘培全;;液晶顯示器用鉬鎢合金接線材料[J];中國鉬業(yè);1996年03期

6 馬捷,畢安園,王從曾,周美玲;化學(xué)氣相沉積制備鉬鎢合金[J];真空科學(xué)與技術(shù)學(xué)報;2005年03期

7 ;綜合信息[J];世界有色金屬;2005年05期

8 ;[J];;年期

相關(guān)碩士學(xué)位論文 前1條

1 楊靜;鉬鎢合金在液鋅中腐蝕的分子動力學(xué)模擬[D];河北工業(yè)大學(xué);2015年

，

本文編號：2035204