本文選題：虹彩釉　切入點(diǎn)：陶瓷磚　出處：《中國陶瓷》2017年03期

【摘要】：研究了氧化氣氛燒成條件下建筑陶瓷釉面磚裝飾用金屬虹彩釉的配方及制備工藝。結(jié)果表明,當(dāng)釉料配方組成為方解石16.81%、鉛熔塊42.02%、高嶺土1.68%、氧化鋅5.88%、氧化銅3.36%、偏釩酸銨6.72%、磷酸鐵10.92%、氧化錳9.24%、鈦白扮2.52%、氧化鈷0.84%,外加0.26%三聚磷酸鈉和0.13%羧甲基纖維素作為添加劑,在噴釉厚度0.6 mm和燒成溫度1180℃的條件下釉面虹彩效果最佳。X-射線衍射分析表明,釉中的主晶相為黑錳礦Mn_3O_4,同時存在CuMn_2O_4、ZnFe_2O_4等尖晶石型晶相。
[Abstract]:The formulation and preparation process of metallic rainbow glaze for decoration of ceramic glazed tiles in oxidized atmosphere were studied.The results showed that when the glaze formula was composed of calcite 16.81, lead nugget 42.02, kaolin 1.68, zinc oxide 5.8810, copper oxide 3.36x, ammonium metavanadate 6.72, iron phosphate 10.92, manganese oxide 9.24, titanium white 2.52, cobalt oxide 0.844, added 0.26% sodium tripolyphosphate and 0.13% carboxymethyl cellulose as additives,Under the conditions of thickness 0.6 mm and firing temperature 1180 鈩，