本文選題：彩色鍍膜玻璃 + 磁控濺射　； 參考：《人工晶體學(xué)報(bào)》2016年05期

【摘要】：經(jīng)過膜系設(shè)計(jì),以TiO_2和SiO_2為介質(zhì)膜,采用磁控濺射鍍膜工藝,制備了不同顏色的鍍膜玻璃,計(jì)算了不同顏色玻璃的色坐標(biāo)。用XPS表征了TiO_2薄膜中Ti元素價(jià)態(tài)以及化學(xué)計(jì)量比;用紫外-可見光譜儀測(cè)試了復(fù)合膜選擇性反射的特性;通過將鍍膜玻璃浸泡于酸、堿中測(cè)試了其環(huán)境穩(wěn)定性。測(cè)試結(jié)果表明,復(fù)合膜具有較強(qiáng)的抗堿能力,但其抗酸腐蝕能力較弱,隨著腐蝕時(shí)間的延長,反射譜線向短波方向漂移且峰值降低;同時(shí),也分析了腐蝕機(jī)理和譜線漂移的原因。
[Abstract]:The coating glass with different colors was prepared by using TiO _ 2 and SiO _ 2 as dielectric films , and the color coordinates of different color glass were calculated by magnetron sputtering coating . The environmental stability of the composite membrane was measured by XPS . The results show that the composite membrane has stronger alkali resistance , but its acid corrosion resistance is weak . As the corrosion time is prolonged , the reflection lines drift toward the short wave direction and the peak value decreases ; meanwhile , the corrosion mechanism and the cause of spectral line drift are also analyzed .

【作者單位】： 武漢理工大學(xué)硅酸鹽建筑材料國家重點(diǎn)實(shí)驗(yàn)室;江蘇秀強(qiáng)玻璃工藝股份有限公司;
【基金】：企業(yè)委托、湖北省重大科技創(chuàng)新計(jì)劃項(xiàng)目(2013AAA005)
【分類號(hào)】：O484.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前8條

1 ;溶膠凝膠鍍膜玻璃[J];中國科技信息;1993年07期

2 潘其真;孟怡敏;張s顂，

本文編號(hào)：1882230