【摘要】：采用甲醛/苯甲醛、苯乙酮和水合肼為原料分別合成了AJ和BJ兩種曼尼希堿緩蝕劑。通過靜態(tài)掛片失重法、電化學(xué)測試法等方法研究了在15%HCl(質(zhì)量分?jǐn)?shù))溶液中,這兩種緩蝕劑對N80鋼的緩蝕性能。結(jié)果表明:在15%的HCl溶液中,AJ和BJ緩蝕劑對N80鋼具有良好的緩蝕作用,且BJ緩蝕劑的緩蝕效果要優(yōu)于AJ緩蝕劑的;兩種緩蝕劑均為陽極型緩蝕劑,都能自發(fā)吸附在N80鋼表面,其行為均符合Langmuir吸附等溫式。
[Abstract]:Using formaldehyde / benzaldehyde, acetophenone and hydrazine hydrate as raw materials, two kinds of Mannich alkali corrosion inhibitors AJ and BJ were synthesized respectively. The results show that AJ and BJ inhibitor have good corrosion inhibition effect on N80 steel in 15% HCl solution, and the inhibition effect of BJ inhibitor is better than that of AJ inhibitor. The two inhibitors are anodic corrosion inhibitors and can be spontaneously adsorbed on the surface of N80 steel. The behavior of the two inhibitors accords with the Langmuir adsorption isotherm.
【作者單位】： 長江大學(xué)化學(xué)與環(huán)境工程學(xué)院;
【基金】：國家自然科學(xué)基金(41202111) 國家大學(xué)生創(chuàng)新實(shí)驗(yàn)計(jì)劃項(xiàng)目(111048910)
【分類號】：TE983

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 李衛(wèi)佳;梁平;;季銨化曼尼希堿的復(fù)配性能研究[J];精細(xì)石油化工進(jìn)展;2011年04期

相關(guān)碩士學(xué)位論文 前1條

1 吳蘭蘭;肼改性為酸化緩蝕劑的研究[D];長江大學(xué);2013年

，

本文編號：1511866