【摘要】：自水泥混凝土問世以來，裂縫問題一直困擾著人們，許多學者試圖用不同的方法解決收縮裂縫。由于長期以來對砂石骨料的研究不大重視，使很多工程中出現(xiàn)的混凝土缺陷難于解釋。因而,本文著重從混凝土的骨料和在混凝土中加入杜拉纖維兩個方面來研究混凝土的性能及其早期裂縫。 本文通過骨料級配分維值的不同和杜拉纖維摻量的不同，研究骨料分維值和杜拉纖維摻量對混凝土力學性能的影響；通過平板試驗，研究杜拉纖維混凝土骨料級配的分形特征及纖維摻量對其早期表面塑性開裂的影響兩個方面。結(jié)果表明: 1．骨料的分維值為2.4的混凝土試塊抗壓強度和抗折強度是最大的，骨料分維對于混凝土的抗壓和抗折強度的影響不同，，所以對于不同分維值混凝土的抗壓強度和抗折強度的走勢不同。 2．杜拉纖維的摻入對混凝土抗折強度的影響明顯優(yōu)于其對抗壓強度的影響，且1.0kg/m~3摻量的效果優(yōu)于0.5kg/m~3摻量的效果。 3．隨著骨料級配分維值的增大，混凝土早期塑性開裂的越嚴重，總開裂面積增大，但是其初裂時間卻越來越長。 4．杜拉纖維對混凝土早期塑性裂縫的抑制有很好的作用。運用分形維數(shù)能夠更直接、明了的對混凝土的早期開裂做出評價。
[Abstract]:Since the advent of cement concrete, the problem of cracks has been puzzling people. Many scholars try to solve shrinkage cracks with different methods. It is difficult to explain the concrete defects in many projects. Therefore, this paper focuses on the performance of concrete and its early cracks from the aspects of concrete aggregate and the addition of Dura fiber in concrete. In this paper, the effects of aggregate fractal dimension and Dura fiber content on the mechanical properties of concrete are studied by using the different fractal dimension of aggregate gradation and the different content of Dura fiber, and the effects of the fractal dimension of aggregate and the content of Dura fiber on the mechanical properties of concrete are studied. The fractal characteristics of aggregate gradation of Dura fiber concrete and the effect of fiber content on early surface plastic cracking are studied. The results show that:. 1. The compressive strength and flexural strength of concrete specimens with a fractal dimension of 2.4 are the largest, and the effects of fractal dimension of aggregate on the compressive and flexural strength of concrete are different. So the compressive strength and flexural strength of concrete with different fractal dimension are different. 2. The effect of the addition of Dura fiber on the flexural strength of concrete is obviously better than that on the compressive strength of concrete, and the effect of 1.0 kg / m ~ (-3) is better than that of 0.5 kg / m ~ (3). 3. With the increase of the fractal dimension of aggregate gradation, the more serious the early plastic cracking of concrete is, the larger the total crack area is, but the longer the initial crack time is. 4. Dura fiber has a good effect on the suppression of early plastic crack of concrete. The fractal dimension can be used to evaluate the early crack of concrete more directly and clearly.
【學位授予單位】：內(nèi)蒙古農(nóng)業(yè)大學
【學位級別】：碩士
【學位授予年份】：2013
【分類號】：TU528.572

【參考文獻】

相關(guān)期刊論文 前10條

1 姜曉偉;宓永寧;高躍;;不同分維骨料級配對混凝土性能影響的研究[J];房材與應用;2006年02期

2 高小建,何忠茂,楊英姿,周智,巴恒靜;周邊約束狀態(tài)下板式混凝土早期開裂及收縮應變的分布[J];硅酸鹽學報;2004年03期

3 李國強,鄧學鈞;級配骨料的分形效應[J];混凝土;1995年01期

4 謝和平,陳至達;巖石類材料裂紋分叉非規(guī)則性幾何的分形效應[J];力學學報;1989年05期

5 謝和平,王金安;巖石節(jié)理(斷裂)表面的多重分形性質(zhì)[J];力學學報;1998年03期

6 孫麗鳳;分形幾何方法模擬混凝土材料的裂紋擴展[J];青島建筑工程學院學報;1998年02期

7 祝文化;李建雄;張明中;;混凝土損傷裂紋的二維數(shù)字圖像盒維數(shù)算法[J];武漢理工大學學報;2008年06期

8 張佚倫;詹樹林;錢曉倩;孟濤;錢匡亮;;聚丙烯纖維混凝土早期收縮性能試驗研究[J];新型建筑材料;2006年01期

9 成盛;金南國;田野;金賢玉;;混凝土裂縫特征參數(shù)的圖形化定量分析新方法[J];浙江大學學報(工學版);2011年06期

10 彭瑞東,謝和平,鞠楊;二維數(shù)字圖像分形維數(shù)的計算方法[J];中國礦業(yè)大學學報;2004年01期

相關(guān)碩士學位論文 前1條

1 王麗;混凝土骨料級配及表面裂縫擴展的分形試驗研究[D];內(nèi)蒙古農(nóng)業(yè)大學;2009年

本文編號：1525783