文獻(xiàn)名稱：前處理對鎂合金化學(xué)鍍鎳結(jié)合力的影響

    前言：研究了鎂合金多種前處理工藝對化學(xué)鍍鎳層與基體之間結(jié)合力的影響.采用彎曲法、銼刀實驗法和劃線劃格實驗3種鍍層結(jié)合力測試方法,對化學(xué)鍍鎳層與鎂合金基體之間結(jié)合力的優(yōu)劣進(jìn)行了定性評價.結(jié)果表明,采用一步法前處理工藝的試樣,鍍層與基體之間具有良好的結(jié)合力,金相顯微觀察發(fā)現(xiàn)鍍層與基體之間具有最薄的中間過渡層.用浸鋅工藝能較好地改善鍍層與基體間的結(jié)合力。但鎂合金浸鋅工藝值得做進(jìn)一步的研究.
    The influences of different pretreatment techniques on the adhesion of electroless nickel plating on magnesium alloy have been studied in this paper.The adhesive force between the coating and the magnesium substrate has been estimated by using bend test,file test,and scribe test.The results indicate that the samples which is one step pretreated has the best adhesion and the thinnest mesosphere between the coating film and magnesium substrate.The adhesive force between the coating and the magnesium substrate...

文獻(xiàn)名稱 前處理對鎂合金化學(xué)鍍鎳結(jié)合力的影響

Article Name
英文(英語)翻譯 INFLUENCE OF PRETREATMENT ON THE ADHESION OF ELECTROLESS NICKEL PLATING ON MAGNESIUM ALLOY;

作者 鄭臻; 余新泉; 孫揚(yáng)善; 薛烽; 任世科;

Author ZHENG Zhen;YU Xinquan;SUN Yangshan;XUE Feng;REN Shike （Department of Materials Science and Engineering;Southeast University;Nanjing 210096）;

作者單位
Author Agencies 東南大學(xué)材料科學(xué)與工程系; 東南大學(xué)材料科學(xué)與工程系 南京;

文獻(xiàn)出處
Article From 中國科學(xué)院上海冶金研究所; 材料物理與化學(xué)(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 鎂合金; 化學(xué)鍍鎳; 前處理; 結(jié)合力; 浸鋅;

Keywords magnesium alloy;electroless nickel planting;pretreatment of substrate;adhesion;zincification;

鎂合金低壓恒流陽極氧化膜研究
鎂合金上二步法電鍍鋅的研究
鎂合金表面化學(xué)轉(zhuǎn)化膜的研究進(jìn)展
累積疊軋工藝對AZ31鎂合金板材組織和性能的影響
Mg-9Sr中間合金的組織及其對AZ31鎂合金組織細(xì)化的影響
ZAC843鎂合金金屬型鑄造組織和力學(xué)性能
AZ91D鎂合金表面機(jī)械研磨處理后顯微結(jié)構(gòu)研究
pH值對AZ 91D鎂合金化學(xué)鍍鎳的影響
AZ 31鎂合金稀土轉(zhuǎn)化成膜及其耐蝕性能的研究
鎂合金化學(xué)鍍Ni-P合金工藝研究現(xiàn)狀

  本文關(guān)鍵詞：前處理對鎂合金化學(xué)鍍鎳結(jié)合力的影響，由筆耕文化傳播整理發(fā)布。