【摘要】：為了研究鋯鈦酸鉛壓電陶瓷燒成用氧化鋁陶瓷承燒板的損壞機制,對在鋯鈦酸鉛壓電陶瓷燒成中使用80次后的氧化鋁陶瓷承燒板的顯微結(jié)構(gòu)和化學組成的變化進行了分析,探討了氧化鋁陶瓷承燒板被侵蝕的過程及發(fā)生翹曲、表面粉化、剝落的原因。研究認為:氧化鋁陶瓷承燒板被鋯鈦酸鉛組分侵蝕,是從其顆粒表面逐漸向顆粒內(nèi)部深入的;碳化硅推板加速了氧化鋁陶瓷承燒板的損壞。鋯鈦酸鉛組分侵入以及承燒板底面生成玻璃相,兩者共同作用,導致了氧化鋁陶瓷承燒板中心凸起翹曲及表面層狀粉化剝落。
[Abstract]:In order to study the damage mechanism of alumina ceramic sintered plate for lead zirconate titanate ceramic sintering, the microstructure and chemical composition of alumina ceramic bearing plate after 80 times firing were analyzed. The process of erosion of alumina ceramic board and the causes of warpage, surface pulverization and spalling are discussed. The results show that the alumina ceramic plate is corroded by lead zirconate titanate from the surface of the particle to the interior of the particle and the silicon carbide plate accelerates the damage of the ceramic board. The intrusion of lead zirconate titanate and the formation of glass phase on the bottom of the sintered plate resulted in the central warping of alumina ceramic board and the surface layer flaking.
【作者單位】： 景德鎮(zhèn)陶瓷大學材料科學與工程學院;
【分類號】：TQ174.65;TQ175.7

【相似文獻】

相關(guān)碩士學位論文 前2條

1 陳仕俊;MMA體系注凝成型低成本制備氧化鋁陶瓷膜及其分離特性研究[D];東華大學;2017年

2 李德鑫;激光表面微織構(gòu)加工及減阻技術(shù)研究[D];寧波大學;2017年

，

本文編號：2134632