本文選題：白炭黑 + 濕法研磨　； 參考：《華東理工大學(xué)學(xué)報(自然科學(xué)版)》2017年01期

【摘要】：提高白炭黑在輪胎橡膠中的分散性,有利于提高輪胎橡膠拉伸強度并降低其滾動阻力。本文利用高速濕法研磨,通過正交試驗研究了研磨過程工藝參數(shù)對白炭黑分散性能的影響。結(jié)果表明鋯球直徑對白炭黑的分散性影響最大,在轉(zhuǎn)速5 000r/min,分散時間80 min,鋯球直徑0.9mm,白炭黑質(zhì)量20g,六偏磷酸鈉(SHMP)質(zhì)量分?jǐn)?shù)2%的條件下白炭黑分散最佳,中位徑(D50)可降至112nm。
[Abstract]:Increasing the dispersity of silica in tire rubber can improve the tensile strength of tire rubber and reduce its rolling resistance. In this paper, the effects of grinding process parameters on the dispersion properties of silica were studied by orthogonal experiment with high speed wet grinding. The results showed that the diameter of zirconium ball had the greatest influence on the dispersity of silica. Under the conditions of rotational speed 5 000 r / min, dispersing time 80 min, zirconium ball diameter 0.9 mm, white carbon black 20 g and sodium hexametaphosphate (SHMP) 2%, the dispersion of silica was the best, and the median diameter (D50) could be reduced to 112 nm.
【作者單位】： 華東理工大學(xué)材料科學(xué)與工程學(xué)院超細(xì)材料制備與應(yīng)用教育部重點實驗室;
【基金】：國家自然科學(xué)基金(91534202,91534122) 上海市基礎(chǔ)重點研究項目(15JC1401300) 國家國際科技合作專項項目(2015DFA51220)
【分類號】：TQ127.2

【參考文獻】

相關(guān)期刊論文 前9條

1 燕鵬華;梁滔;;白炭黑改性及其在橡膠中的應(yīng)用研究進展[J];橡膠科技;2015年10期

2 張立;王禮;王廷山;戴圣佳;劉振鋒;;白炭黑及其分散劑的發(fā)展及在輪胎中的應(yīng)用[J];橡膠工業(yè);2015年09期

3 陳婉婷;丁浩;曹麗;羅琴;崔程琳;;機械研磨對水介質(zhì)中白炭黑顆粒解聚和分散的影響[J];中國粉體技術(shù);2015年03期

4 景允伸;許宏;常華;張香蘭;;成核階段對沉淀法白炭黑團聚程度的影響[J];山東化工;2015年09期

5 曹麗;崔程琳;陳婉婷;丁浩;;沉淀法白炭黑顆粒在水介質(zhì)中的解聚與分散研究[J];非金屬礦;2014年06期

6 辛?xí)跃?;白炭黑在輪胎中的應(yīng)用及其研究進展[J];廣東化工;2012年11期

7 鄭麗華;劉欽甫;程宏飛;;白炭黑表面改性研究現(xiàn)狀[J];中國非金屬礦工業(yè)導(dǎo)刊;2008年01期

8 張慶軍,莫文玲,王占樂;沉淀法制備納米白炭黑的結(jié)構(gòu)及性質(zhì)的研究[J];硅酸鹽通報;2005年04期

9 王軍民,王夏冰;球磨過程中粉末的行為變化[J];甘肅工業(yè)大學(xué)學(xué)報;1999年01期

【共引文獻】

相關(guān)期刊論文 前10條

1 陳鵬宇;周梅芳;姜海波;李春忠;;沉淀法白炭黑的分散性[J];華東理工大學(xué)學(xué)報(自然科學(xué)版);2017年01期

2 薛兵;楊�？�;王百年;葛禮響;王仲漢;;氟硅酸廢水制備白炭黑的改性研究[J];化工新型材料;2017年02期

3 席e，

本文編號：2073281