本文選題：透光混凝土 + 力學(xué)性能��； 參考：《混凝土》2017年09期

【摘要】：透光混凝土是一種新型建筑材料。為滿足建筑行業(yè)的需求,對透光混凝土制備工藝、性能進行深入透徹地研究已變得非常迫切。對透光混凝土的力學(xué)性能、耐久性能,以及其光學(xué)性能進行了研究,研究表明:透光混凝土的力學(xué)性能與摻入光纖的種類,光纖的摻量密切相關(guān)。不論摻入有機玻璃(PMMA)或者聚苯乙稀(PS)光纖,光纖的摻入明顯提高體系的抗壓強度,隨著光纖摻量的增加,體系抗壓強度先增加后減少。光纖的摻入可以明顯提高體系的抗裂性能,且隨著光纖摻量的增加脆性系數(shù)降低。對于同一齡期,同種光纖摻量條件下,PS組的試件脆性系數(shù)大于PMMA組的試件。光纖的摻入降低了透光混凝土的抗硫酸侵蝕性能和抗氯離子滲透性能,隨著光纖摻量的增加,抗硫酸侵蝕性能和抗氯離子滲透性能降低。隨著光纖摻量的增加,透光率明顯增加。PS光纖的試件的透光率略低于PMMA試件,但相差不大。
[Abstract]:Transparent concrete is a new type of building material. In order to meet the needs of the construction industry, it has become very urgent to study the properties of transparent concrete. The mechanical properties, durability and optical properties of transparent concrete are studied. The results show that the mechanical properties of transparent concrete are closely related to the type of doped fiber and the content of optical fiber. The compressive strength of the system was obviously increased with the addition of PMMA (PMMA) or PS). With the increase of fiber content, the compressive strength of the system first increased and then decreased. The addition of fiber can improve the crack resistance of the system, and the brittleness coefficient decreases with the increase of fiber content. For the same age, the brittleness coefficient of PS group is higher than that of PMMA group under the same fiber content. The sulfuric acid corrosion resistance and chloride ion permeation resistance of transparent concrete decreased with the addition of optical fiber, and the sulfuric acid corrosion resistance and chloride ion permeability decreased with the increase of fiber content. With the increase of fiber content, the transmittance of PS fiber is slightly lower than that of PMMA sample, but the difference is not significant.
【作者單位】： 中建商品混凝土有限公司;
【基金】：中建股份科技研發(fā)課題(CSCEC-2015-Z-56)
【分類號】：TU528.38

【相似文獻】

相關(guān)期刊論文 前10條

1 包亦望;孫立;邱巖;;陶瓷力學(xué)性能綜合評價技術(shù)與分析軟件[J];稀有金屬材料與工程;2009年S2期

2 Helga Szibor;Hans W.Hennicke;王振林;徐如恬;;瓷材料的顯微結(jié)構(gòu)數(shù)據(jù)與力學(xué)性能之間的關(guān)系(第Ⅱ部分)[J];中國電瓷;1984年04期

3 包亦望;;陶瓷及玻璃力學(xué)性能評價的一些非常規(guī)技術(shù)[J];硅酸鹽學(xué)報;2007年S1期

4 楊巍屹;馬南鋼;;3YPSZ-Al_2O_3-Co_3O_4陶瓷力學(xué)性能的研究[J];中國陶瓷;2012年12期

5 也冰;;風(fēng)擋安全玻璃光學(xué)性能的檢驗[J];玻璃;1988年03期

6 杜金成,林文輝,趙修建,劉文,方羅珍;含銀偏振玻璃的制備及光學(xué)性能[J];光學(xué)學(xué)報;1999年05期

7 ;混凝土家族新成員——生態(tài)友好型混凝土[J];中國水利;2006年20期

8 魏超平;對嵌裝式裝飾石膏板力學(xué)性能的研究[J];新型建筑材料;1996年03期

9 聶麗華;馮輝榮;林潔榮;羅仁安;樊建超;;綠化混凝土的植物相容性及亞熱帶草種選擇[J];新型建筑材料;2006年03期

10 付強,周萘,黃文e，

本文編號：1995858