本文選題：水泥 + 熟料特性��； 參考：《筑路機械與施工機械化》2017年05期

【摘要】：為了進一步研究銅礦尾礦用于制備水泥熟料的可行性,采用銅礦尾礦替代砂巖燒制水泥熟料。通過f-CaO測試分析銅礦尾礦制備水泥熟料的易燒性,同時借助XRD測試水泥熟料中成分比例,最后對銅礦尾礦制備水泥熟料的凝結(jié)時間及力學性能進行了驗證。結(jié)果表明:升高煅燒溫度更有利于使用銅礦尾礦制備水泥熟料;用銅礦尾礦替代砂巖可降低f-CaO,但熟料的礦物晶體結(jié)晶度下降,且C3S礦物燒成率略偏低,凝結(jié)時間、早期強度與普通水泥熟料相差不大。
[Abstract]:In order to further study the feasibility of using copper tailings to prepare cement clinker, copper tailings were used instead of sandstone to make cement clinker. The burnability of cement clinker prepared by copper tailings was analyzed by f-CaO test, and the composition ratio of cement clinker was measured by XRD. Finally, the setting time and mechanical properties of cement clinker prepared by copper tailings were verified. The results show that increasing the calcination temperature is more favorable for the preparation of cement clinker from copper tailings, and replacing sandstone with copper tailings can reduce f-CaO, but the crystallinity of clinker is decreased, and the sintering rate of C3S mineral is slightly lower and the setting time is lower. The early strength of cement clinker is not different from that of ordinary cement clinker.
【作者單位】： 山西省交通規(guī)劃勘察設計院;
【基金】：山西省交通運輸廳科技項目(2015-1-26) 山西省交通建設科技項目(2015-2-04)
【分類號】：TQ172.1

【相似文獻】

相關期刊論文 前10條

1 朱紀明;關于加快國投水泥二線建設的建議[J];中國建材;2001年02期

2 胡錫泉;利廢生產(chǎn)水泥熟料[J];建材工業(yè)信息;2003年01期

3 謝華林,李坦平;等離子發(fā)射光譜法測水泥熟料中的多元素[J];水泥;2003年07期

4 ;2004年2月重點聯(lián)系水泥企業(yè)產(chǎn)、銷、存情況[J];中國建材;2004年04期

5 本刊編輯部;《新型干法燒成水泥熟料設備設計、制造、安裝與使用》[J];四川水泥;2004年03期

6 ;2008年1月重點聯(lián)系水泥企業(yè)產(chǎn)、銷、存、價情況[J];中國建材;2008年03期

7 周鴻錦;;水泥產(chǎn)量增速減緩 需求呈現(xiàn)下降征兆[J];中國水泥;2008年11期

8 馬秋忠;;2011年元月重點聯(lián)系水泥企業(yè)產(chǎn)、銷、存、價分析[J];中國水泥;2011年03期

9 ;2013年1月重點聯(lián)系水泥企業(yè)產(chǎn)、銷、存、價分析[J];中國建材;2013年03期

10 王家治;鍶水泥、捛水泥與，

本文編號：1970420