本文選題：氧化銀電極 + 鋅銀貯備電池��； 參考：《電源技術》2017年09期

【摘要】：采用幾種化成制度制備了氧化銀電極和鋅電極,以恒流極化、單體手動激活放電和組合電池自動激活放電實驗考察了電極的電性能;采用掃描電子顯微鏡(SEM)和化學分析對氧化銀電極的表面形態(tài)和組分進行了表征。結(jié)果表明,氧化銀電極放電初期極化大是影響電池組激活時間的主要因素,也是造成電池放電初期電壓上升緩慢的主要原因,9 m A/cm2轉(zhuǎn)6、3 m A/cm2的階梯充電模式有利于提高電池激活速度。
[Abstract]:Silver oxide electrode and zinc electrode were prepared by several chemical processes. The electrical properties of the electrode were investigated by constant current polarization, manual activation discharge of monomer and automatic activation discharge of combined battery. The surface morphology and composition of silver oxide electrode were characterized by scanning electron microscopy (SEM) and chemical analysis. The results show that the large polarization in the initial discharge of silver oxide electrode is the main factor affecting the activation time of the battery pack. It is also the main reason that the voltage rise slowly in the initial discharge stage of the battery. The stepwise charging mode of 9 m A/cm2 to 6 m A/cm2 is helpful to improve the activation speed of the battery.
【作者單位】： 中國電子科技集團公司第十八研究所;
【分類號】：TM911

【相似文獻】

相關期刊論文 前6條

1 關抗芳;;新法制備銀—硫化銀電極[J];杭州化工;1983年01期

2 陳勝利，吳秉亮，楊漢西;電化學石英晶體微天平對銀電極氧化還原過程的研究[J];高等學�；瘜W學報;1994年01期

3 王琪山,黃秀貞,王瑾;PTC陶瓷歐姆接觸銀電極的研究[J];電子元件與材料;1993年03期

4 付秀芝,陳玲君,汪葆浚;銀電極絡合電位法測定鍍鉻液中SO_4~(2-)的含量[J];華東化工學院學報;1985年03期

5 顏志明;自動電位滴定法測定水中氯離子[J];環(huán)境監(jiān)測管理與技術;1997年02期

6 廖孟生，，呂鑫，張乾二;相對論密度泛函法對CN~－在銅和銀電極上振動頻率的研究[J];電化學;1995年03期

相關碩士學位論文 前2條

1 王曉春;在金銀電極上電解二氧化碳制備一氧化碳的研究[D];昆明理工大學;2015年

2 張永光;貯備式鋅—銀電池氧化銀電極的電化學性能研究[D];哈爾濱工業(yè)大學;2011年

本文編號：1955274