本文選題：飛機除冰液 + 普通混凝土��； 參考：《湖南大學(xué)學(xué)報(自然科學(xué)版)》2017年11期

【摘要】：結(jié)合現(xiàn)有的凍融破壞理論,研究了以乙二醇為主要成份的飛機除冰液作用下普通混凝土凍融損傷失效規(guī)律與特點.采用X射線衍射儀、掃描電子顯微鏡和X射線能量色散譜儀,進(jìn)行試件凍融后的物相組成、微觀結(jié)構(gòu)變化以及微區(qū)元素分析.實驗結(jié)果表明:低質(zhì)量分?jǐn)?shù)乙二醇對混凝土抗凍剝蝕性比水嚴(yán)重,高質(zhì)量分?jǐn)?shù)乙二醇對混凝土的凍融破壞比水輕微.飛機除冰液質(zhì)量分?jǐn)?shù)越低,對混凝土的凍融破壞作用越嚴(yán)重;低質(zhì)量分?jǐn)?shù)乙二醇對普通混凝土的凍融破壞以表面剝落破壞為主,質(zhì)量損失首先達(dá)到破壞標(biāo)準(zhǔn).高質(zhì)量分?jǐn)?shù)乙二醇對普通混凝土的凍融破壞以相對動彈性模量首先達(dá)到破壞標(biāo)準(zhǔn),主要表現(xiàn)為端部的嚴(yán)重凍疏.在乙二醇飛機除冰液凍融過程中普通混凝土內(nèi)沒有新物質(zhì)生成,水化硅酸鈣凝膠與氫氧化鈣晶體未發(fā)生變化.普通混凝土在乙二醇飛機除冰液中的凍融破壞機理與水中一樣,以結(jié)冰壓破壞為主.
[Abstract]:Combined with the existing freeze-thaw failure theory, the failure law and characteristics of freeze-thaw damage of ordinary concrete under the action of aircraft deicing liquid with ethylene glycol as the main component are studied. X-ray diffractometer, scanning electron microscope and X-ray energy dispersive spectrometer were used to analyze the phase composition, microstructure and microelements of the samples after freezing and thawing. The experimental results show that the low mass fraction ethylene glycol is more serious than water in frost and denudation, and the freeze-thaw damage of high mass fraction ethylene glycol is less than that of water. The lower the mass fraction of the aircraft deicing fluid, the more serious the freeze-thaw failure of concrete, and the more serious the freeze-thaw failure of ordinary concrete caused by low mass fraction ethylene glycol is the surface spalling failure, and the mass loss first reaches the damage standard. The freezing and thawing failure of ordinary concrete caused by high mass fraction ethylene glycol first reaches the failure standard with the relative dynamic elastic modulus, which is mainly shown as the severe freezing and thinning at the end of the concrete. In the freeze-thaw process of ethylene glycol aircraft deicing fluid, there is no new substance formed in ordinary concrete, and the hydrated calcium silicate gel and calcium hydroxide crystal do not change. The freezing and thawing failure mechanism of ordinary concrete in ethylene glycol aircraft deice is the same as that in water.
【作者單位】： 南京航空航天大學(xué)航空宇航學(xué)院;南京航空航天大學(xué)金城學(xué)院;北京古城房地產(chǎn)開發(fā)有限公司;江蘇省交通科學(xué)研究院股份有限公司;
【基金】：國家重點基礎(chǔ)研究發(fā)展計劃(973計劃)資助項目(2015CB655100) 國家自然科學(xué)基金資助項目(51178221,21276264,51308304) 高性能土木工程材料國家重點實驗室重點基金項目(2015CEM001)~~
【分類號】：TU528

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 陳琳;;淺談普通混凝土在施工中的配合比設(shè)計[J];民營科技;2013年02期

2 王春杰;楊娜;;談建筑用普通混凝土的組成材料[J];民營科技;2012年05期

3 梅措;;關(guān)于普通混凝土的耐久性分析[J];城市建筑;2013年12期

4 李宏斌;;普通混凝土高性能化淺析[J];門窗;2012年12期

5 孫帥;王立文;;飛機除冰液快速換熱器設(shè)計[J];機床與液壓;2010年08期

6 李文生;王美莉;楊寧;;再生集料混凝土與普通混凝土的凍融性研究[J];工程建設(shè);2010年03期

7 萬麗紅;張樹華;;淺談混凝土強度檢驗評定標(biāo)準(zhǔn)的變化[J];山西建筑;2011年15期

8 趙卓;曾力;郝志超;;基于不確定性的氯離子侵蝕環(huán)境下普通混凝土結(jié)構(gòu)的耐久性研究[J];混凝土;2012年08期

9 李東方;;淺談普通混凝土配合比設(shè)計中的若干問題[J];內(nèi)蒙古水利;2006年01期

10 張松;;普通混凝土配合比設(shè)計應(yīng)注意的幾個問題[J];現(xiàn)代城市軌道交通;2013年03期

，

本文編號：1833350