本文選題：真空冶金 + WC-Co硬質(zhì)合金廢料��； 參考：《有色金屬(冶煉部分)》2017年12期

【摘要】：通過熱力學(xué)計(jì)算,從理論上分析了1 550~2 000℃、壓力小于1.73Pa的條件下,采用真空冶金法可以從WC-Co硬質(zhì)合金廢料中分離WC硬質(zhì)相和鈷黏結(jié)相。隨后,以鈷含量為3%~15%的WC-Co硬質(zhì)合金廢料為原料進(jìn)行了鈷含量對鈷揮發(fā)率、純度以及對WC粉末質(zhì)量影響的研究。結(jié)果表明,鈷揮發(fā)率隨原料鈷含量的增大先增大后減小,鈷含量為8%時(shí)鈷揮發(fā)率達(dá)最大值86.63%;原料鈷含量對金屬鈷的純度無明顯規(guī)律性影響,鈷含量為12%時(shí)金屬鈷純度達(dá)最大值99.95%。WC粉末的XRD譜顯示,當(dāng)原料鈷含量為3%和15%時(shí)出現(xiàn)鈷衍射峰,有鈷殘留,原料鈷含量為5%、8%及12%時(shí)未出現(xiàn)鈷衍射峰,各次試驗(yàn)均未出現(xiàn)W2C相,無明顯脫碳;WC粉末的SEM形貌顯示,粉末呈近球形,表面光滑,粒徑為1~8μm。試驗(yàn)制得了合格WC粉末和金屬鈷。
[Abstract]:The cobalt content of WC - Co cemented carbide was studied by thermodynamic calculation . The results showed that the cobalt content of WC - Co cemented carbide was up to 86.63 % when the cobalt content was 3 % and 15 % , and the cobalt content was 8 % . The cobalt content was about 5 % , the cobalt content was 5 % , the cobalt content was 8 % and 12 % . The results showed that the cobalt content was about 5 % , the cobalt content was 5 % , the cobalt content was 8 % and 12 % . The results showed that the cobalt content was about 5 % , the cobalt content was 5 % , the cobalt content was 8 % and 12 % .

【作者單位】： 國家鎢與稀土產(chǎn)品質(zhì)量監(jiān)督檢驗(yàn)中心;江西省鎢與稀土產(chǎn)品質(zhì)量監(jiān)督檢驗(yàn)中心;江西省鎢與稀土研究院;
【分類號(hào)】：TF816;TQ136.13

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 李秋霞;荊碧;尹琦;陳為亮;戴永年;;真空冶金法直接從磷礦石制備紅磷的新思路[J];化工礦物與加工;2007年11期

相關(guān)碩士學(xué)位論文 前1條

1 肖杰;旋轉(zhuǎn)密封閥的設(shè)計(jì)研究[D];鋼鐵研究總院;2017年

，

本文編號(hào)：1759202