本文選題：有機(jī)玻璃　切入點(diǎn)：粘接縫　出處：《硅酸鹽通報(bào)》2017年04期

【摘要】：測試了由四種粘接工藝(常規(guī)粘接、快料粘接、常溫紫外光固化粘接和升溫紫外光固化粘接)制備的有機(jī)玻璃粘接縫試樣的抗拉強(qiáng)度;應(yīng)用Weibull分布理論分析了四組試樣抗拉強(qiáng)度數(shù)據(jù)的分散性。研究表明:Weibull分布函數(shù)能夠很好地描述有機(jī)玻璃粘接縫的強(qiáng)度分布;快料粘接工藝制備的粘接縫試樣平均強(qiáng)度較高,粘接系數(shù)為0.83,且粘接過程耗時(shí)短,較適用于大型工程中有機(jī)玻璃結(jié)構(gòu)的拼接。
[Abstract]:The tensile strength of an organic glass bonded joint prepared by four bonding processes ( conventional bonding , fast adhesive bonding , normal temperature ultraviolet curing adhesion and temperature rise ultraviolet curing adhesion ) was tested . The Weibull distribution theory was applied to analyze the dispersion of the tensile strength data of the four groups of specimens . The results show that the Weibull distribution function can describe the strength distribution of the bond joint of the PMMA . The results show that the average strength of the adhesive joint sample prepared by the fast material bonding process is higher , the bonding coefficient is 0.83 , and the bonding process is short time , and is suitable for splicing of the organic glass structure in large engineering .

【作者單位】： 浙江大學(xué)化工機(jī)械研究所;中國科學(xué)院高能物理研究所;
【基金】：中國科學(xué)院戰(zhàn)略性先導(dǎo)科技專項(xiàng)(A類)項(xiàng)目(XDA10010200)
【分類號】：TQ171.68

【相似文獻(xiàn)】

相關(guān)期刊論文 前5條

1 金宗哲,馬眷榮,汪林生;結(jié)構(gòu)陶瓷彎曲強(qiáng)度的Weibull統(tǒng)計(jì)實(shí)驗(yàn)研究[J];硅酸鹽學(xué)報(bào);1990年02期

2 白世鴻,陳彥,喬生儒,陳玉順,康沫狂;SiC陶瓷高溫彎曲強(qiáng)度的Weibull模量研究[J];機(jī)械強(qiáng)度;2000年04期

3 王恒武,王繼輝,黃再滿,朱京楊;用Weibull評價(jià)表面處理對玻璃纖維強(qiáng)度影響[J];武漢理工大學(xué)學(xué)報(bào);2003年06期

4 許崇海,艾興,黃傳真,劉健;Weibull模數(shù)與陶瓷刀具可靠性[J];濟(jì)南大學(xué)學(xué)報(bào)(綜合版);1997年02期

5 ;[J];;年期

相關(guān)碩士學(xué)位論文 前1條

1 傅滟;等靜壓成型99氧化鋁陶瓷及其抗折強(qiáng)度的Weibull分析[D];濟(jì)南大學(xué);2014年

，

本文編號：1726879