本文選題：應力腐蝕　切入點：疲勞　出處：《材料保護》2017年09期

【摘要】：某化工廠工藝管線上的316不銹鋼材質的孔板流量計導壓管斷裂,導致介質泄漏發(fā)生火災。為查明其失效原因,對斷裂的儀表管進行成分、硬度、金相、斷口形貌和腐蝕產(chǎn)物分析,確認儀表管發(fā)生斷裂的原因是在安裝應力、震動和環(huán)境中Cl元素的共同作用下,先發(fā)生了應力腐蝕形成裂紋源,裂紋達到門檻值后又以疲勞形式擴展,最終導致開裂。
[Abstract]:The orifice plate Flowmeter tube of 316 stainless steel material on the process pipeline of a chemical plant is broken, which results in the fire of medium leakage.In order to find out the failure reason, the composition, hardness, metallography, fracture appearance and corrosion product of the broken instrument tube are analyzed. It is confirmed that the reason of the fracture of the instrument tube is under the joint action of installation stress, vibration and Cl element in the environment.The crack source is formed by stress corrosion first, the crack reaches the threshold value and then propagates in the form of fatigue, which leads to the crack finally.
【作者單位】： 中國石油獨山子石化分公司壓力容器檢驗所;中國石油獨山子石化分公司機動處;中石油西部管道公司工程項目管理部;中國石油獨山子石化分公司儲運聯(lián)合車間;
【分類號】：TQ056.15

【相似文獻】

相關期刊論文 前10條

1 金敏;;《應力腐蝕研究》即將出版[J];南京工業(yè)大學學報(自然科學版);1985年01期

2 沈保羅,馮可芹,高升吉;鈦合金的應用和應力腐蝕[J];四川化工與腐蝕控制;2000年02期

3 徐國元;應力腐蝕原因及對策淺析[J];精細化工中間體;2001年04期

4 閆鳳芹;夏智富;;硫化氫應力腐蝕原理與防護措施[J];煉油與化工;2009年01期

5 于士淋;;氨管道在工程設計中預防應力腐蝕的研究[J];當代化工;2011年09期

6 ;關于催化吸收解吸系統(tǒng)的腐蝕氫滲透和應力腐蝕問題[J];勝利石油化工;1978年02期

7 成長齡;;高壓設備的應力腐蝕及防腐措施[J];河南化工;1980年02期

8 李中柱;;壓力容器應力腐蝕爆破事故分析[J];山東化工學院學報;1981年01期

9 魯濤;魏滬蘭;;涂漆金屬抗硫化氫應力腐蝕的研究[J];井礦鹽技術;1981年01期

10 任凌波;;壓力容器的應力腐蝕及其防護[J];遼寧化工;1982年04期

相關重要報紙文章 前1條

1 韓明德;九江石化化肥合成氨裝置導壓管堵漏成功[N];經(jīng)理日報;2006年

相關碩士學位論文 前4條

1 張杰;18-8系不銹鋼管線和法蘭腐蝕失效與研究[D];大連理工大學;2016年

2 李國帥;S32168不銹鋼在氯離子環(huán)境中的應力腐蝕研究[D];山東大學;2013年

3 范士義;00Cr17Ni14MO3鋼乙醛精餾塔底接管失效研究[D];大慶石油大學;2006年

4 劉清;波紋管熱網(wǎng)加熱器失效研究[D];大慶石油學院;2003年

，

本文編號：1700744