本文選題：蒸壓加氣混凝土　切入點(diǎn)：外墻板　出處：《鄭州大學(xué)》2015年碩士論文　論文類型：學(xué)位論文

【摘要】：蒸壓加氣混凝土(autoclaved aerated lightweight concrete)作為一種新型墻體材料,由于其在輕質(zhì)、防火、易于施工、經(jīng)濟(jì)性等方面較為突出而備受關(guān)注,但是在作為外墻板的實(shí)際應(yīng)用過程中,多孔、吸水快的特征對(duì)外墻板的結(jié)構(gòu)性能、保溫性能影響較大并且缺乏相關(guān)方面的系統(tǒng)研究等原因限制了非承重ALC外墻板的應(yīng)用,因此有必要對(duì)“含水率對(duì)非承重ALC外墻板基本性能的影響”進(jìn)行深入的、系統(tǒng)的研究。通過對(duì)不同含水率狀態(tài)下ALC砌塊的力學(xué)性能、ALC板的保溫性能指標(biāo)的研究,提出了針對(duì)非承重ALC外墻板的結(jié)構(gòu)性能、保溫性能的研究,并且在材料的力學(xué)性能、保溫性能的基礎(chǔ)上建立ANSYS結(jié)構(gòu)性能分析模型、保溫性能理論分析模型,綜合結(jié)構(gòu)性能、保溫性能確定合理板厚,為非承重ALC外墻板的利用提供參考。本文的研究工作主要包括以下幾個(gè)方面:說明了本文的研究背景和選題意義;闡述了非承重ALC外墻板的利用研究現(xiàn)狀,并指出了目前應(yīng)用研究中存在的主要問題;對(duì)非承重ALC外墻板試件的材料進(jìn)行了不同含水率下的力學(xué)基本性能試驗(yàn)(抗壓強(qiáng)度試驗(yàn)、劈裂抗拉強(qiáng)度、靜力受壓彈性模量)和保溫性能試驗(yàn)(導(dǎo)熱系數(shù)、熱阻),分析了含水率對(duì)力學(xué)基本性能和保溫性能的影響;通過ALC材料的基本性能試驗(yàn)研究不同含水率下的非承重ALC外墻板的結(jié)構(gòu)性能和保溫性能,并通過ANSYS14.0分析模擬不同板厚的板的結(jié)構(gòu)性能;通過結(jié)構(gòu)性能和保溫性能試驗(yàn)結(jié)果和有限元分析結(jié)果確定非承重ALC外墻板的合理板厚。
[Abstract]:Autoclaved aerated lightweight concrete (autoclaved aerated concrete), as a new type of wall material, has attracted much attention because of its light weight, fire resistance, ease of construction, economy and so on, but it is porous in the practical application of outer wall. The structural properties of the external wall panels with fast water absorption, the thermal insulation performance and the lack of systematic research on the related aspects restrict the application of the non-load-bearing ALC outer wall panels. Therefore, it is necessary to make a deep and systematic study on the effect of moisture content on the basic properties of non-load-bearing ALC outer wall panels. Through the study on the mechanical properties of ALC blocks under different moisture content and the thermal insulation performance index of ALC panels, The structural properties and thermal insulation properties of non-load-bearing ALC outer wall panels are studied. On the basis of the mechanical properties and thermal insulation properties of the materials, the structural performance analysis model of ANSYS, the theoretical analysis model of thermal insulation performance and the comprehensive structural properties are established. The heat preservation property determines the reasonable board thickness, provides the reference for the use of the non-load-bearing ALC outer wall panel. The research work of this paper mainly includes the following aspects: explain the research background of this paper and the significance of selecting the topic; In this paper, the present situation of the application of non-load-bearing ALC outer wall panel is described, and the main problems in the application research are pointed out, and the basic mechanical properties (compressive strength test) of the non-load-bearing ALC outer wall panel are tested under different moisture content. Splitting tensile strength, static compressive elastic modulus) and thermal insulation performance test (thermal conductivity, thermal resistance, analysis of moisture content on the mechanical properties and thermal insulation properties; The structural properties and thermal insulation properties of non-load-bearing ALC outer wall panels with different moisture content were studied by the basic performance tests of ALC materials, and the structural properties of the panels with different thickness were simulated by ANSYS14.0 analysis. The reasonable plate thickness of the non-load-bearing ALC outer wall is determined by the test results of structural performance and thermal insulation performance and the finite element analysis results.
【學(xué)位授予單位】：鄭州大學(xué)
【學(xué)位級(jí)別】：碩士
【學(xué)位授予年份】：2015
【分類號(hào)】：TU528

【相似文獻(xiàn)】

相關(guān)期刊論文 前3條

1 張波;李建新;;建筑工業(yè)化裝配式外墻板的選擇[J];廣東建材;2013年07期

2 易美濟(jì);;建筑師的最佳選擇:千思板國際Meteon外墻板又推新品[J];國外塑料;2006年06期

3 ;[J];;年期

相關(guān)會(huì)議論文 前6條

1 諶萌;;粉煤灰可以制造內(nèi)、外墻板[A];纖維水泥制品行業(yè)纖維增強(qiáng)水泥及其制品論文選集（1）（1960～2009）[C];2009年

2 紀(jì)瑞星;王慶華;封葉;曲圣英;;輕質(zhì)復(fù)合保溫外墻板的研究及應(yīng)用[A];吉林省土木建筑學(xué)會(huì)2012年學(xué)術(shù)年會(huì)論文[C];2012年

3 李漢周;趙孟彬;;外墻板板縫滲漏的綜合治理[A];全國防水技術(shù)經(jīng)驗(yàn)交流會(huì)暨第四屆防水技術(shù)專業(yè)委員會(huì)學(xué)術(shù)年會(huì)論文集[C];1997年

4 朱松超;楊志毅;;GRC外墻板的設(shè)計(jì)研究[A];纖維水泥制品行業(yè)纖維增強(qiáng)水泥及其制品論文選集（1）（1960～2009）[C];2009年

5 趙艷華;王東斌;;淺談新里程“PC樓”的技術(shù)應(yīng)用[A];土木建筑學(xué)術(shù)文庫（第9卷）[C];2008年

6 毛義平;;地下室外墻板裂縫產(chǎn)生的原因和防止裂縫產(chǎn)生的技術(shù)措施[A];混凝土工程結(jié)構(gòu)裂縫控制與混凝土新技術(shù)交流會(huì)論文集[C];1999年

相關(guān)重要報(bào)紙文章 前4條

1 駐廣東記者 方箏 通訊員 伍國瑞;佳堡外墻板被國家體育館工程采用[N];中國建材報(bào);2008年

2 陳安德;建筑設(shè)計(jì)施工——做好防水的基礎(chǔ)[N];中國建材報(bào);2010年

3 大力;千思板“變色龍”金屬色外墻板創(chuàng)意無限[N];中國建材報(bào);2006年

4 伍國瑞;廣東佳堡外墻板中標(biāo)國家體育館[N];中國建材報(bào);2007年

相關(guān)碩士學(xué)位論文 前8條

1 袁彬;嵌入式基礎(chǔ)疊合式地下室外墻板平面外抗彎性能試驗(yàn)研究[D];合肥工業(yè)大學(xué);2015年

2 葉松;預(yù)制復(fù)合保溫外墻板的性能研究[D];安徽建筑大學(xué);2016年

3 朱國陽;預(yù)制混凝土建筑外墻設(shè)計(jì)初探[D];南京工業(yè)大學(xué);2016年

4 趙端鋒;聚丙烯纖維稻殼砂漿外墻板性能試驗(yàn)研究[D];武漢輕工大學(xué);2016年

5 王海強(qiáng);含水率對(duì)非承重ALC外墻板基本性能影響的試驗(yàn)研究[D];鄭州大學(xué);2015年

6 許德峰;裝配式剪力墻結(jié)構(gòu)外墻板問題研究[D];沈陽建筑大學(xué);2013年

7 孫泉;鋼結(jié)構(gòu)住宅中煤矸石輕骨料混凝土外墻板系的研究[D];太原理工大學(xué);2007年

8 黃莉;嵌入式基礎(chǔ)的疊合式地下室外墻板的平面外受彎性能試驗(yàn)和ANSYS參數(shù)分析[D];合肥工業(yè)大學(xué);2014年

，

本文編號(hào)：1644707