本文選題：溶膠-凝膠　切入點：水凝膠　出處：《上海應(yīng)用技術(shù)學(xué)院》2015年碩士論文　論文類型：學(xué)位論文

【摘要】：納米二氧化鈦作為一種功能材料,具備一系列優(yōu)良的性能。由于二氧化鈦中存在晶體缺陷,為氧空位存在提供了條件,其作為催化劑受到了越來越多的關(guān)注。本文采用溶膠一凝膠法、水凝膠模板法制備出了納米二氧化鈦,采用微流控制備出了二氧化鈦微球,并比較了它們負載氧化銅之后的催化性能。采用正交試驗的方法制備出不同配比下的凝膠,根據(jù)正交試驗發(fā)現(xiàn)了水解抑制劑是影響鈦酸四丁酯水解的主要因素,丙烯酸做抑制劑時凝膠時間比乙酸做抑制劑時長,且制備出的晶粒直徑更小；抑制劑的加入延緩了晶相的轉(zhuǎn)變抑制了晶粒的長大。采用水凝膠模板法制備出了納米二氧化鈦,在制備過程中,有效的抑制了鈦酸四丁酯的水解,在水凝膠未吸水之前沒有或只有很少量的鈦酸四丁酯水解。討論了影響微流控前驅(qū)體溶液穩(wěn)定性的因素—丙烯酰胺的用量、硝酸的加入量和加水量。選用聚乙二醇/聚丙烯酸前驅(qū)體溶液合成的微球,制備的Ti02微球尺寸均勻,球形度較好,但焙燒后微球表面比較粗糙。XRD分析表明Ti02微球的晶粒尺寸10nm,晶體結(jié)構(gòu)為銳鈦礦相。測定了銳鈦礦催化氧化一氧化碳的活性,發(fā)現(xiàn)銳鈦礦型二氧化鈦具有催化活性,但是不高。制備了負載氧化銅的催化劑,比較了各個催化劑的催化活性。
[Abstract]:Nano titanium dioxide as a kind of functional material, has a series of excellent performance. Due to the presence of crystal defects in titanium dioxide, provided the conditions for the existence of oxygen vacancies, the catalyst has attracted more and more attention. This paper adopts the method of sol-gel, hydrogel template method prepared nanometer titanium dioxide was prepared by micro flow control TiO2 microspheres and their catalytic performance of supported copper oxide. After preparation by orthogonal test method was prepared under different ratio of the gel, according to orthogonal test found that hydrolysis inhibitors are the main factors influencing the hydrolysis of titanium acid butyl ester four, acrylic acid as inhibitor gel time inhibitors than acetic acid, and the prepared the grain diameter is smaller; inhibitors added delay phase shift inhibit grain growth. The hydrogel template prepared two nanometer titanium dioxide, In the preparation process, effectively inhibited the hydrolysis of four butyl titanate, no water or not before the hydrogel with only a small amount of four butyl titanate hydrolysis. The paper discusses the factors affecting the microfluidic precursor solution stability of acrylamide, nitrate content and water content. The polyethylene glycol / polyacrylic acid precursor solution the synthesis of microspheres, preparation of Ti02 microspheres with uniform size, good sphericity, but after roasting microspheres with rough surface.XRD analysis showed that the grain size of 10nm Ti02 microspheres, the crystal structure of anatase anatase. The catalytic oxidation of carbon monoxide were investigated, found that anatase TiO2 with catalytic activity, but not the high load oxidation catalyst. Copper was prepared and compared the catalytic activity of different catalysts.

【學(xué)位授予單位】：上海應(yīng)用技術(shù)學(xué)院
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2015
【分類號】：TQ134.11;TB383.1

【相似文獻】

相關(guān)期刊論文 前10條

1 鄭元昌;使用催化氧化工藝從工廠廢水中回收醋酸[J];化工生產(chǎn)與技術(shù);2003年02期

2 韓東;陳孟林;黃智;何星存;;吸附-催化氧化再生技術(shù)處理廢水的研究進展[J];化工技術(shù)與開發(fā);2011年08期

3 羅貴昌;;多元催化氧化處理化纖廢水的研究[J];河南化工;2011年15期

4 羅忠鑒 ,楊盛書 ,桂正良;化學(xué)演示實驗的研究和改革Ⅲ氨的催化氧化[J];四川師院學(xué)報(自然科學(xué)版);1981年01期

5 張紹芳;對氨的催化氧化演示實驗的改進[J];西南師范學(xué)院學(xué)報(自然科學(xué)版);1984年03期

6 徐永福;二氧化硫在大氣含水體系中的催化氧化[J];應(yīng)用化學(xué);1987年05期

7 張福芝;杭道耐;;苯和丁烷催化氧化制順酐的氣相色譜分析[J];化學(xué)工業(yè)與工程;1988年02期

8 宮寶安;王孝昒;李長海;;含硫脫毛堿膨脹廢水的催化氧化治理[J];環(huán)境污染與防治;1989年04期

9 陳先明,胡寶妹,程衛(wèi)平,孟小玲;催化氧化葡萄糖制備葡萄糖酸鈉和D-葡萄糖酸δ-內(nèi)酯[J];化學(xué)世界;1990年05期

10 郭國瑞;袁們，

本文編號：1586635