本文關(guān)鍵詞： 氧化石墨烯 水泥基材料 水泥基體 水泥水化晶體 微觀結(jié)構(gòu) 建筑用化學(xué)品　出處：《精細(xì)化工》2016年05期 　論文類型：期刊論文

【摘要】：為了解決氧化石墨烯(GO)納米片層在水泥基體中的分散問題,制備了丙烯酸(AA)、丙烯酰氧乙基三甲基氯化銨(AAC)和丙烯磺酸鈉(SAS)的共聚物(PAAS),PAAS與GO納米片層形成PAAS/GO復(fù)合物并顯示出分散作用。結(jié)果表明,w(PAAS)=2%分別與w(GO)=0.01%、0.02%和0.03%形成的復(fù)合物可使水泥基體分別形成由花狀晶體、多面體狀晶體和針狀晶體構(gòu)成的規(guī)整有序的微觀結(jié)構(gòu),28 d時的抗折強(qiáng)度分別比對照樣提高了63.0%、90.4%和87.9%,抗壓強(qiáng)度分別提高了32.6%、74.2%和71.3%,同時這些水化晶體容易生長在裂縫、孔洞等缺陷處,具有修復(fù)結(jié)構(gòu)缺陷的效果。PAAS通過與GO納米片層形成復(fù)合物實(shí)現(xiàn)了GO在水泥基材料中的均勻分散以及對水泥基材料微觀結(jié)構(gòu)和性能的調(diào)控。
[Abstract]:In order to solve the dispersion problem of graphene oxide nanocrystalline (GOO) in cement matrix, The copolymers of acryloxyethyl trimethylammonium chloride (Acryloxyethyl trimethylammonium chloride) and sodium Acrylsulfonate (Sas) were prepared to form PAAS/GO complexes with go nanolamellae and show dispersion. The cement matrix can be formed separately by flower-like crystals, The flexural strength of polyhedron crystal and needle-like crystal is increased by 63.00.44% and 87.9%, respectively, and the compressive strength is increased by 32.64.2% and 71.3%, respectively, and the hydrated crystals are easy to grow in cracks, compared with the normal microstructure of acicular crystal for 28 d. The flexural strength of polyhedron crystal and acicular crystal is increased by 63.00.40% and 87.9% respectively, and the compressive strength is increased by 32.64.2% and 71.3%, respectively. Paas has the effect of repairing structural defects. Paas realizes the homogeneous dispersion of go in cement-based materials and the regulation of microstructure and properties of cement-based materials by forming a complex with go nanoscale.
【作者單位】： 陜西科技大學(xué)資源與環(huán)境學(xué)院;
【基金】：國家自然科學(xué)基金(21276152)~~
【分類號】：TQ172.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前3條

1 陽知乾;劉建忠;劉加平;李長風(fēng);周華新;;化學(xué)沉積法改善纖維-水泥基體的界面性能[J];建筑材料學(xué)報;2013年04期

2 陶錦范;提高玻璃纖維耐堿性的途徑[J];玻璃纖維;1996年03期

3 ;[J];;年期

相關(guān)會議論文 前1條

1 崔艷玲;崔琪;崔玉忠;;火山灰材料對硅酸鹽水泥基體GRC耐久性的影響[A];纖維水泥制品行業(yè)纖維增強(qiáng)水泥及其制品論文選集（1）（1960～2009）[C];2009年

，

本文編號：1529634