本文關(guān)鍵詞： 廢棄砂漿粉 抗凍性能 水灰比 抗壓強度 質(zhì)量損失　出處：《混凝土》2017年08期 　論文類型：期刊論文

【摘要】：研究了廢棄砂漿粉對混凝土抗凍性的影響,測試了不同水灰比及廢棄砂漿粉摻量下凍融循環(huán)后混凝土的抗壓強度、質(zhì)量損失。結(jié)果表明,隨著凍融次數(shù)增加,混凝土的質(zhì)量損失率及抗壓強度損失率增大,當水灰比低于0.44時,經(jīng)25次凍融后,混凝土抗壓強度略有升高;隨著廢棄砂漿摻量增加,混凝土的抗凍性能總體呈下降趨勢,試驗范圍內(nèi),當水灰比低于0.44時,廢棄砂漿粉摻量低于10%,可以提高混凝土抗凍性能。隨著水灰比增加,相同條件下,混凝土的質(zhì)量損失率及抗壓強度損失率均呈增大趨勢。
[Abstract]:The influence of waste mortar powder on the frost resistance of concrete is studied. The compressive strength and mass loss of concrete under freeze-thaw cycle under different water / cement ratio and waste mortar powder content are tested. The results show that with the increase of freezing and thawing times, the compressive strength and mass loss of concrete under freeze-thaw cycle are measured. The mass loss rate and compressive strength loss rate of concrete increase. When the water-cement ratio is lower than 0.44, the compressive strength of concrete increases slightly after 25 times freeze-thaw. In the range of test, when the ratio of water to cement is lower than 0.44, the content of waste mortar powder is less than 10, and the frost resistance of concrete can be improved. With the increase of water-cement ratio, the loss rate of mass and compressive strength of concrete increases with the increase of water-cement ratio.
【作者單位】： 沈陽建筑大學材料科學與工程學院;
【基金】：“十二五”國家科技支撐計劃課題(2013BAJ15B03) 國家建筑材料行業(yè)科技創(chuàng)新計劃(2013-M3-8) 住房和城鄉(xiāng)建設部項目(2015-K4-002)
【分類號】：TU528

【相似文獻】

相關(guān)期刊論文 前5條

1 要秉文,宋少民,高振國;砌抹砂漿粉的試制與應用[J];石家莊鐵道學院學報;1999年04期

2 呂建福;巴恒靜;譚憶秋;;海洋黏細菌對砂漿滲透性和微觀結(jié)構(gòu)影響[J];建筑材料學報;2013年04期

3 閆玉蓉;方永浩;龔泳帆;承禮清;;堿激發(fā)再生水泥砂漿粉膠凝材料的強度與顯微結(jié)構(gòu)[J];材料導報;2013年24期

4 要秉文,羅永會,于躍勛;MC砂漿粉的開發(fā)[J];粉煤灰綜合利用;2000年02期

5 錢寶軍;楊瑩;;高含碳粉煤灰球磨后在混凝土和砂漿中的應用研究[J];商品混凝土;2014年01期

相關(guān)會議論文 前1條

1 邱建華;蔣俊輝;劉小泉;;聚氨酯保溫板系統(tǒng)中水泥玻纖界面黏結(jié)砂漿的性能研究[A];第五屆全國商品砂漿學術(shù)交流會論文集（5th NCCM）[C];2013年

，

本文編號：1496960